The effect of coatings on the interfacial strength of a hollow glass microsphere/polyester composite and their capacity to endure thermal stresses were studied by mechanical testing and an active Acoustic Emission (AE) method. AE was postulated to provide more local information at or near the glass/polyester interface due to the sensitivity of elastic waves to the rigidity of polymer chains at the glass sphere/polyester interface compared to mechanical testing.
Three frequency ranges identified by multivariate statistics yet consolidated for the initial analysis into a band of 140-240 kHz, were found to be changing with the different coated glass filler for different glass content and heating state. Considering the acoustic behavior of the composites containing different levels of glass sphere content (1-10 vol%), a lower concentration (aminoethylamino)-propyl-trimethoxy silane coated glass (AS6), demonstrated the lowest attenuation after heating (associated with higher interfacial strength). As anticipated, the highest attenuation after heating was observed for uncoated glass (16K) due to expectedly weaker associations. Mechanical testing results after heating were consistent with the AE response for AS6 and 16K for this frequency range. Trends in amplitude for the three narrower, frequency ranges of 130-160 kHz, 180-220 kHz and 230-260 kHz were compared against that of 140-240 kHz and very small differences were observed. It was found that the frequency range of 130-60 kHz was more descriptive of the changes of interfacial strength in composites (at 10 vol%), being consistent with the mechanical test results. Considering the AE response at 130-160 kHz and mechanical data, higher concentration (aminoethylamino)-propyl-trimethoxy silane (AS12), better endured thermal stresses compared to other coatings. A smaller trial looked at the effect of moisture aging and subsequent thermal cycling on the glass/polymer interface strength as another method to perturb the interface. Attenuation for the band of 180-260 kHz was studied for aged versus non-aged composites. The commercial coating, L21 demonstrated a better moisture resistance before and after thermal cycling compared to uncoated glass spheres.
An improved evaluation of interfacial strength in glass/polyester was expected using AE technique versus mechanical testing due to its higher sensitivity to changes in internal structure, however; no significant improvement compared to mechanical testing was observed, at least based on the analysis technique currently being used. / Thesis / Master of Applied Science (MASc) / Sheet molded compound (SMC) is a polymer material reinforced by fibers providing a combination of light weight and high mechanical properties and is used in automotive industry. Light weight fillers (hollow glass microspheres) are used to obtain further weight reduction; however, addition of these fillers leads to reduced mechanical properties and further problems during painting process known as ‘paint popping’. The former is due to uncertain interfacial state between polymer and fillers and the latter results from different thermal expansion behavior of the polymer and filler materials while the material is exposed to high temperatures for painting process. This research aims to devise a highly sensitive technique and evaluate its suitability compared to mechanical testing for investigation of the origin of aforementioned problems. Acoustic Emission (AE) is a method with high sensitivity to changes in internal structure of the material which is postulated to provide a better insight on material microstructure compared to more commonly used method i.e. mechanical testing. Use of interfacial controlling agents was examined to reduce the problems as a result of introduction of fillers. The effect of using surface modified fillers and the effect of thermal stresses on material was investigated using AE technique. Application of AE method in this study provided a good insight about the changes in material internal structure; however, it did not demonstrate a significant improvement in detecting the origins of studied problems compared to mechanical testing at least based on the analysis technique used in this study.
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/19024 |
| Date | January 2016 |
| Creators | Mousavi Khalkhali, Zeinab |
| Contributors | Thompson, Michael, Chemical Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0021 seconds