The thermal plasma production of fumed silica in a transferred arc consists of the decomposition of quartz to SiO (g) and oxygen followed by an oxidizing quench back to SiO2. The particles formed have diameters of the order of 10 to 20 nm and are linked in a three dimensional branched chain aggregate. Previous work by Addona and Munz (1999) demonstrated the technical feasibility of producing fumed silica using this method, but was unable to demonstrate the special rheological properties of the powder. The most important characteristic of fumed silica is the presence of hydroxyls on the surface of the particles, in the form of isolated hydroxyl groups, hydrogen-bonded hydroxyl groups and siloxane groups. / In the present work, we studied the changes in the powder quality by varying the quench conditions used for the production of the powder and by agglomerating the obtained particles. The fumed silica was agglomerated by conveying in a length of tubing with sharp bends. The powder was characterized using BET, Viscosity tests, FT-IR, TEM, SEM and XRD. The product was compared to both a commercial product (Aerosil 200) and the material previously produced by Addona. Tests were done before and after the agglomeration experiments. / The experimental results showed that the agglomeration had no effect on the powder's rheological properties. We concluded that the smaller viscosity values obtained for the plasma produced fumed silica were due to the lack of the free hydroxyl groups from the surface of the particles.
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:QMM.99787 |
Date | January 2006 |
Creators | Pristavita, Ramona. |
Publisher | McGill University |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Format | application/pdf |
Coverage | Master of Engineering (Department of Chemical Engineering.) |
Rights | © Ramona Pristavita, 2006 |