Orientador: Maria do Carmo Gonçalves / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-05T15:56:25Z (GMT). No. of bitstreams: 1
Segatelli_MarianaGava_M.pdf: 3623345 bytes, checksum: 223789f87f6234b864c485f4c771efa2 (MD5)
Previous issue date: 2005 / Resumo: O objetivo principal deste trabalho foi avaliar a incorporação de fibras curtas de sílica (FS) e da borracha etileno-propileno-dieno funcionalizada com anidrido maleico (EPDM-g-AM) em polimérica de poliamida 6 (PA 6). A fibra utilizada como carga é um produto natural constituído de sílica amorfa proveniente da fossilização de animais multicelulares. Com a finalidade de promover a melhor adesão interfacial entre a fibra e a matriz polimérica, as fibras foram modificadas com aminopropiltrietoxissilano (APTS), um agente de acoplamento. Os materiais foram preparados em extrusoras monorosca e duplarosca e, submetidos a ensaios mecânicos de tração, flexão e de impacto Izod. Foram também avaliadas as características térmicas e morfológicas desses materiais. As fibras de sílica não alteraram a estabilidade térmica da PA 6 e apresentaram eficiência de reforço, dentro do intervalo de composição estudado; entretanto, o alongamento na ruptura foi comprometido. A resistência ao impacto do polímero não variou significativamente com a incorporação de FS. Por outro lado, o tipo de extrusora utilizada para processamento alterou a cristalinidade da PA 6 e, conseqüentemente, as propriedades mecânicas nos compósitos binários de PA 6/FS. A modificação da superfície da fibra com APTS não foi adequada para melhorar as propriedades mecânicas, no entanto, a análise da microestrutura dos compósitos obtidos indicou adesão entre as fases. Em relação às blendas de PA 6/EPDM-g-AM, o tamanho médio de partícula da fase dispersa promoveu um efeito de tenacificação da PA 6. Os compósitos ternários de PA 6 contendo 20% de EPDM-g-AM e proporções diferentes de FS (5 a 20%) apresentaram redução na resistência ao impacto quando pequenas quantidades de FS foram adicionadas. Apesar da redução no valor desta propriedade, os compósitos obtidos exibiram boa tenacidade. Desta forma, a combinação de fibras curtas de sílica e borracha de EPDM-g-AM em poliamida 6 permitiu recuperar parcialmente a rigidez e a resistência ao impacto, que são comprometidas quando esses aditivos são utilizados separadamente. / Abstract: The main goal of this work was to evaluate the incorporation of short silica fibers (SF) and ethylene-propylene-diene rubber, functionalized with maleic anhydride (EPDM-g-MA), in a polyamide 6 (PA 6) matrix. The fiber used as filler is a natural product made up of amorphous silica from the fossilization of multicelular animals. In order to promote a better interfacial adhesion between the fiber and the polymeric matrix, fibers were modified with the aminopropyltriethoxysilane (APTS) coupling agent. The materials were prepared in single and twin-screw extruders for tensile, flexural and Izod impact mechanical tests. The mechanical, morphological and thermal properties of these materials were evaluated. Silica fibers did not change the thermal stability of the polymer and presented efficiency for reinforcement. However, the elongation at break was impaired. The impact strength of the polymer did not change significantly with the SF content. On the other hand, the type of extruder used for processing changed the mechanical properties and the crystallinity of PA 6 in the PA 6/SF binary composites. The fiber surface modification with APTS was not effective, as verified by the decrease of the mechanical properties. The morphology of composites showed adhesion between the phases. Taking into account the PA 6/EPDM-g-MA blends, the average size of dispersed phase, associated to impact strength in the 20% EPDM-g-MA composition promoted a toughening effect of the blends. Ternary PA 6 composites containing 20% EPDM-g-MA and different SF amounts (5-20%) presented tendency towards the reduction of the impact strength when small SF amounts were added. In spite of the reduction in the value of this mechanical property, the composites obtained exhibited good toughness. Thus, combining short silica fibers and EPDM-g-MA rubber with polyamide 6, the stiffness and the impact strength, that are impaired when these additives are separately used, were partially recovered. / Mestrado / Físico-Química / Mestre em Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248718 |
| Date | 26 July 2005 |
| Creators | Segatelli, Mariana Gava |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gonçalves, Maria do Carmo, 1957-, Junior, Elias Hage, Yoshida, Inez Valéria Pagotto |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 94 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds