>Magister Scientiae - MSc / The growth of hydrogenated amorphous silicon carbide (a-SiC:H) thin films deposited by Hot- Wire Chemical Vapour Deposition (HWCVD) for solar cell applications has been studied. The films were characterized for structural properties using Fourier Transform Infrared Spectroscopy FTIR, Elastic Recoil Detection Analysis (ERDA), X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM) and Raman Spectroscopy (RS). A low temperature of the substrate heater maintained at 280 °C was used in this thesis due to the demand of low-cost solar cells based on cheap substrate that require deposition at such low temperatures. In this thesis, we showed that the structural properties of a-SiC:H films are dependent on the filament temperature and also on the CH4 gas flow rate. It was shown that in non-stoichiometric a-SiC:H, hydrogen content throughout the deposited films varies with depth. An attempt is done in this study to determine, for the first time the absorption strength of the C-Hn bonds in the 950 -1050 cm-1 band of the FTIR spectrum. Real-time ERDA was used to determine the hydrogen kinetics parameters in a single temperature ramp; a model based on the solution of the diffusion equation is used for this effect.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:uwc/oai:etd.uwc.ac.za:11394/4345 |
| Date | January 2014 |
| Creators | Khoele, Joshua Relebogile |
| Contributors | Halindintwali, S., Julies, B. |
| Publisher | University of the Western Cape |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Rights | University of the Western Cape |
Page generated in 0.0025 seconds