Desenvolvimento de suporte catalítico monolítico para fins aeroespaciais empregando a manufatura aditiva / Monolithic catalytic support development for aerospace applications employing additive manufacture

No presente trabalho foi desenvolvido um suporte catalítico monolítico para fins aeroespaciais empregando a manufatura aditiva. Para tanto, foi proposta uma geometria que proporcione um escoamento turbulento, permitindo um maior contato entre o reagente e a superfície do catalisador, proporcionando menor perda de carga ao sistema. Esta nova estrutura foi obtida via manufatura aditiva, através da técnica de Sinterização Seletiva a Laser (SLS) indireta. Para utilizar a técnica SLS e material cerâmico, foi necessário desenvolver um revestimento sobre as partículas de alumina para promover a aderência entre as mesmas durante o processo de manufatura aditiva. Em seguida foram definidos, experimentalmente, os parâmetros de aplicação da técnica SLS para o compósito alumina/poliamida. Por fim, foi fabricado, via SLS, o suporte catalítico na forma monolítica. Após a confecção do suporte monolítico, foi desenvolvido um revestimento composto de pseudo-boemita e nitrato de alumínio e aplicado na superfície do monólito, a fim de expandir a área superficial específica do material. Este aumento da área específica favorece a dispersão da fase ativa, composta de óxidos de cobalto e manganês, na superfície do suporte. A caracterização do catalisador monolítico foi realizada a partir das técnicas de Adsorção de Nitrogênio, Análise Termogravimétrica, Microscopia Eletrônica de Varredura e Espectrometria de Emissão Ótica com Fonte de Plasma (ICP-OES). O desempenho do catalisador monolítico na decomposição do H2O2 concentrado foi analisado via teste de gota, monitorado por câmera de alta velocidade. Os bons resultados obtidos nesta reação apontam esta técnica de obtenção de suporte catalítico monolítico através da manufatura aditiva como uma metodologia promissora a ser empregada em sistemas catalíticos com elevada difusão de massa e calor, mas principalmente em sistemas propulsivos a monopropelente. / This work was developed by the additive manufacture monolithic catalytic support to apply aerospace applications. A geometry was proposed to implement a turbulent flow allowing a better contact with catalytic surface and reagent with a low pressure drop in the system. This new structure was obtained by additive manufacture through indirect Selective Laser Sintering (SLS) technique. Firstly, in order to use the SLS for the ceramic material was developed a coating on the alumina particles to promote a melting between them during addictive manufacturing process. Secondly, the printer parameters SLS was configurated into the alumina/polyamide particle. Finally, the monolithic catalytic support was built via SLS. After the monolithic support building, the pseudo-boehmite and aluminum nitrate coating was developed and applied on the monolithic surface to increase the specific superficial area of the material. This increasing of the specific surface area helps the spread of the active phase to made up of cobalt and manganese oxide in the support surface. The characterization of the monolithic catalyst was carried out using the nitrogen adsorption technique, thermogravimetric analysis, scanning electron microscopy and inductive coupled plasma with optical emission spectrometry. The monolithic catalytic performance in the H2O2 concentrated decomposition was analyzed via drop test monitored by the high-speed camera. The good results of this reaction and such a technique of monolithic catalytic support obtainment through the additive manufacture show that a promising methodology can be used in the catalytic system with high diffusion of mass and heat but mainly, in monopropellant propulsive system.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-04122018-143447
Date20 July 2018
CreatorsOliveira, Isaias de
ContributorsVernilli Junior, Fernando, Vieira, Ricardo
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0031 seconds