Previous issue date: 2005 / Os elevados custos das obras de engenharia civil induzem a necessidade de se desenvolver estudos de processos de estabilização e reforço que possibilitem melhorar determinadas propriedades geotécnicas dos solos, de modo a enquadrá-los dentro das especificações construtivas vigentes. A técnica de reforço de solos através da inclusão de fibras tem sido estudada por vários pesquisadores, e tem se mostrado eficiente, melhorando várias propriedades de engenharia do solo, gerando um compósito bastante atraente para a engenharia geotécnica, que neste trabalho será denominado fibrossolo. A avaliação do efeito da adição de fibras de sisal ao solo laterítico foi feita experimentalmente, em laboratório, determinando-se o comportamento mecânico via ensaios de compactação (na energia do Proctor Normal) e CBR, bem como sua resistência ao cisalhamento, através do ensaio de cisalhamento direto. Adotou-se como ponto de partida para análise, os teores de fibra de 0,25% a 1,0% em função da massa seca do solo e, também, do comprimento das fibras, nos valores 10 a 25mm. O trabalho teve como objetivo complementar o estudo do efeito do tratamento superficial das fibras de sisal com poliestireno expandido (EPS) reciclado, visando sua aplicabilidade como elemento inibidor do processo de absorção de água. Com base nos resultados obtidos neste trabalho, notou-se que a adição de fibras de sisal tratadas de distribuição aleatória apresentou significativas melhorias nas propriedades mecânicas do solo laterítico, transformando-o em um produto de melhor qualificação para aplicação em obras de engenharia civil, e que o polímero utilizado mostrou-se bastante aplicado à análise proposta, promovendo diminuição da higroscopicidade das fibras de sisal. ____________________________________________________________________________________________________ / ABSTRACT: The high costs of the civil engineering construction requires the necessity to develop studies about the process of the stabilization and reinforcement which improves some geotechnical soils properties being part of the constructive specifications. The reinforcement technique of the soils with the inclusion of natural fibers has been studied for many researchers. It has showing efficient by improving many properties of the soil engineering which results in an interesting composite material for the geotechnical engineering. This composite is named fibersoil at this research. Experiments was done at the laboratory to evaluate the effect of the addition sisal fibers in the lateritic soil which will establish the mechanical behavior of the material through compaction tests, at the energy of the Normal Proctor and CBR. The shear strength was done through the direct shear test. Therefore, in the present investigation sisal fiber was randomly included in to the soil at four different percentages of fiber content with 0,25% to 1% by weight of raw soil and also considered different lengths between 10 to 25mm. The objective of this research is to contribute to the study on the effect of the sisal fibers with superficial treatment with recycled expanded polystyrene (EPS) inhibiting the absorption of water. With base in the results obtained in this work, it was noticed that the addition treated sisal fibers randomly distributed presented significant improvements in the mechanical properties of lateritic soil, transforming it in a product of better qualification for application in works of civil engineering, and that the polymer used it was shown quite applied to the proposed analysis, promoting decrease of the water absorption of the sisal fibers.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/2550 |
Date | January 2005 |
Creators | Leocádio, Gislene Aparecida Santiago |
Contributors | Botaro, Vagner Roberto |
Publisher | Programa de Pós-Graduação em Engenharia de Materiais. Rede Temática em Engenharia de Materiais, Pró-Reitoria de Pesquisa e Pós-Graduação, Universidade Federal de Ouro Preto. |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFOP, instname:Universidade Federal de Ouro Preto, instacron:UFOP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds