Thermoporosimetry is a technique to determine small pore sizes based on melting and crystallization point depression. The temperature shift was measured by Differential Scanning Calorimetry (DSC). Development of thermoporosimetry was carried out on silica with a well-characterized narrow pore size distribution. Several parameters were studied, which a have a direct influence on melting and crystallization point depression (for example: a quality of the solvent, filling the pores with the solvent, time and frequency of centrifuging, superfluous solvent removal conditions, etc.). The optimum conditions for the thermoporosimetry method were developed using high porosity silica. The optimized experimental conditions found for silica were applied to polypropylene powder with much lower porosity. Several polypropylene powders were synthesized using different polymerization catalysts and their porosity determined. Polymer powder morphology and structure was characterized by standard methods. Powder porosity obtained by thermoporometry, gas sorption, and BET methods was compared.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216874 |
| Date | January 2012 |
| Creators | Urbánková, Radka |
| Contributors | Salajka,, Zdeněk, Kratochvíla, Jan |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds