Master's thesis deals with evaluating applicability of correlation relationships between material characteristics determined by Small Punch Test and standard tensile test for material AlSi7Mg0,6 manufactured by casting and technology SLM. Results of Small Punch Tests are correlated with yield strength, tensile strength, elongation, and Young's modulus of elasticity. For each material characteristic various correlation methods are compared, while for each method corresponding coefficients are determined. Consequently, the applicability of individual methods is evaluated by substituting coefficients determined by various studies. Primarily analyzed are correlation methods for which future normalization is expected. The results of master's thesis show that structural inhomogeneity caused by SLM process does not result in high inaccuracies in determining material characteristics. Larger impact on material characteristics has high porosity, which was identified in cast material and led to significant deviations in evaluating tensile strength and elongation.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:417140 |
| Date | January 2020 |
| Creators | Gordiak, Michal |
| Contributors | Řehořek, Lukáš, Válka, Libor |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Slovak |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds