Previous issue date: 2014-08-29 / Neste estudo foi testada a hipótese de que instrumentos endodônticos
fabricados com a liga de NiTi com tratamento térmico M-Wire são mais resistentes à
corrosão em solução de NaOCl. Avaliou-se, por ensaio de polarização
potenciodinâmica, a resistência à corrosão de 14 limas de NiTi sem tratamento de
superfície (ProTaper® Universal Finishing 2 – F2, n = 7 e Mtwo® 25.07, n = 7) e de 14
limas de NiTi com tratamento de superfície (Reciproc® R25 25.08, n = 7 e Wave-
One® Primary 25.08, n = 7), quando imersas em solução irrigante de NaOCl a
5,25%. Em miscroscópio eletrônico de varredura, as micromorfologias das 28 limas
testadas foram analisadas antes e após o ensaio eletroquímico. As curvas de
polarização anódica foram obtidas com potencial de varredura que iniciou no Ecorr de
cada lima, com uma taxa de 0,333 mV/segundos (1,2 V/hora) até os Epite, sendo
considerada como faixa passiva, a região onde os valores de potencial tinham
densidade de corrente inferior a 10-5 A/cm2. A fim de se comparar as médias dos
grupos aos pares foi empregada a prova não paramétrica de Mann-Whitney,
utilizando-se o software estatístico SPSS-15 e o nível de significância adotado foi de
p < 0,05. As curvas de polarização anódica demonstraram que todas as limas
testadas foram passíveis de corrosão na solução de NaOCl a 5,25% (pH = 6,5).
Observou-se que, no geral, apenas entre as limas Mtwo® (sem tratamento térmico) e
Reciproc® (com tratamento térmico) não houve diferença estatisticamente
significante para Epite ECS e Epite-Ecorr (p = 1,000). Ao se comparar, aos pares, as
limas sem tratamento térmico (ProTaper® Universal F2 e Mtwo®) com as limas com
tratamento térmico (Reciproc® e Wave-One®) não houve diferença estatisticamente
significante (Ecorr ECS, p = 1,000; Epite ECS, p = 0,265; Epite-Ecorr, p = 0,265). A lima
Reciproc® foi a que se apresentou mais resistente à corrosão e a ProTaper® foi a
lima que mais sofreu corrosão na solução testada. Assim, a hipótese inicial de que
instrumentos endodônticos fabricados com a liga de NiTi com tratamento térmico MWire
são mais resistentes à corrosão em solução de NaOCl foi negada. / This study tested the hypothesis that endodontic instruments
manufactured with the NiTi alloy heat treated M-Wire are more resistant to corrosion
in NaOCl solution. Was evaluated by potentiodynamic polarization test, the corrosion
resistance of NiTi files 14 without surface treatment (Universal ProTaper® Finishing 2
- F2, n = 7 and Mtwo® 25.07, n = 7) and 14 files NiTi with surface treatment (R25
Reciproc® 25.08, n = 7 and Primary Wave-One® 25.08, n = 7), when immersed in
irrigating solution of NaOCl 5.25%. In electronic scanning microscopy, the
micromorfologies of 28 tested files analyzed before and after the electrochemical
test. The anodic polarization curves obtained by scanning the potential Ecorr that
initiated in each file with a rate of 0.333 mV/sec (1.2 V/minute) to the Epite, being
considered passive track, the region where the values potential had density of less
than 10-5 A/cm2 current. In order to compare the averages of the groups in pairs used
to non-parametric Mann-Whitney test, using the SPSS-15 statistical software and the
significance level was p < 0.05. The anodic polarization curves show that all tested
files are liable to the corrosion solution of 5.25% NaOCl (pH = 6.5). It was observed
that, in general, only between Mtwo® (without heat treatment) and Reciproc® (heat
treated) files there was no statistically significant difference for Epite ECS and Epite-
Ecorr (p = 1.000). When comparing in pairs, the files without heat treatment
(ProTaper® Universal F2 and Mtwo®) with files with heat treatment (Reciproc® and
Wave-One®) there was no statistically significant difference (Ecorr ECS, p = 1.000;
Epite ECS, p = 0.265; Epite-Ecorr, p = 0.265). The Reciproc® file introduced more
resistant to corrosion and the ProTaper® was the file that suffered most corrosion in
the tested solution. Thus, the initial hypothesis that endodontic instruments
manufactured with the NiTi heat treated M-Wire are more resistant to corrosion in a
solution of NaOCl was refused.
| Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/1356 |
| Date | 29 August 2014 |
| Creators | Costa, Tatiana Dias |
| Contributors | Carmo, Antônio Márcio Resende do, Silva, Elison da Fonseca e, Guimarães, Simone Maria Ragone |
| Publisher | Universidade Federal de Juiz de Fora, Programa de Pós-graduação em Clínica Odontológica, UFJF, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds