Visible-blind and solar-blind ultraviolet photodetectors based on GaN/AlGaN were designed, fabricated, and characterized for commercial and military applications. High performance back-illuminated solar-blind MSM achieved external quantum efficiency of ~48%. The dark current of 40x40μm MSM was less than the instrument measurement limitation of 20fA for a bias <100V. No photoconductive gain was observed. With an n-type doped high-Al ratio "window" Al₀.₆Ga₀.₄N layer, back-illuminated solar-blind p-i-n photodiode achieved a quantum efficiency of ~55% at zero-bias. Absorption edge study of both MSM and p-i-n photodetectors, based on device spectral responses, resulted in a performance comparison of MSMs and p-i-ns, as the solar-blind photodetection requires a sharp solar-blind rejection. Photoconductive detectors and avalanche photodetectors, with the internal gain advantage, have been discussed as well. A 30μm diameter GaN avalanche photodiode achieved a gain >23, with a dark current less than 100pA. The breakdown showed a positive temperature coefficient of 0.03 V/K that is characteristic of avalanche breakdown. SiC APDs, as candidates for visible-blind applications, have been designed, fabricated and characterized. An avalanche gain higher than 10⁵, with a dark current less than 1nA, showed the potential of SiC APD replacing PMTs for high sensitivity visible-blind UV detection. A silicon-based optical receiver has been presented in the Appendix. With the photodiode internal avalanche gain ~4, a sensitivity ~-6.9dBm at 10Gbps has been achieved. / text
| Identifer | oai:union.ndltd.org:UTEXAS/oai:repositories.lib.utexas.edu:2152/29863 |
| Date | 14 May 2015 |
| Creators | Yang, Bo, active 21st century |
| Source Sets | University of Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Format | electronic |
| Rights | Copyright is held by the author. Presentation of this material on the Libraries' web site by University Libraries, The University of Texas at Austin was made possible under a limited license grant from the author who has retained all copyrights in the works. |
Page generated in 0.0023 seconds