Double layer capacitors owe their large capacitance to high specific surface area carbon-based electrode materials adhered to a current collector via an adhesive. However, recent studies attribute greater electrical energy storage capacity to transition metal oxides/nitrides: a new generation of electrode materials for use in super-capacitors with mixed double-layer and pseudo-capacitive properties.
Solution precursor plasma spray deposition is a technique that allows coatings to be fabricated with fine grain sizes, high porosity levels, and high surface area; characteristics ideal for application as super-capacitor electrodes. This investigation established conditions for deposition of porous, high specific surface area α-MoO3. It further identified a two-step temperature-programmed reaction for topotactic phase transformation of the α-MoO3 deposits into high specific surface area molybdenum nitrides of higher conductivity and higher electrochemical stability window. The electrochemical behavior of molybdenum oxide/nitride deposits was also studied in order to assess their potential for use in super-capacitors.
| Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/30608 |
| Date | 07 December 2011 |
| Creators | Golozar, Mehdi |
| Contributors | Coyle, Thomas W. |
| Source Sets | University of Toronto |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0016 seconds