Previous issue date: 2012-08-30 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Nowadays, the use of chemicals that satisfactorily meet the needs of
different sectors of the chemical industry is linked to the consumption of
biodegradable materials. In this context, this work contemplated
biotechnological aspects with the objective of developing a more
environmentally-friendly corrosion inhibitor. In order to achieve this goal,
nanoemulsion-type systems (NE) were obtained by varying the amount of
Tween 80 (9 to 85 ppm) a sortitan surfactant named polyoxyethylene (20)
monooleate. This NE-system was analyzed using phase diagrams in which the
percentage of the oil phase (commercial soybean oil, codenamed as OS) was
kept constant. By changing the amount of Tween 80, several polar NE-OS
derived systems (O/W-type nanoemulsion) were obtained and characterized
through light scattering, conductivity and pH, and further subjected to
electrochemical studies. The interfacial behavior of these NE-OS derived
systems (codenamed NE-OS1, S2, S3, S4 and S5) as corrosion inhibitors on
carbon steel AISI 1020 in saline media (NaCl 3.5%) were evaluated by
measurement of Open Circuit Potential (OCP), Polarization Curves (Tafel
extrapolation method) and Electrochemical Impedance Spectroscopy (EIS). The
analyzed NE-OS1 and NE-OS2 systems were found to be mixed inhibitors with
quantitative efficacy (98.6% - 99.7%) for concentrations of Tween 80 ranging
between 9 and 85 ppm. According to the EIS technique, maximum corrosion
efficiency was observed for some tested NE-OS samples. Additionaly to the
electrochemical studies, Analysis of Variance (ANOVA) and Principal
Component Analysis (PCA) were used, characterization of the nanoemulsion
tested systems and adsorption studies, respectively, which confirmed the
results observed in the experimental analyses using diluted NE-OS samples in
lower concentrations of Tween 80 (0.5 1.75 ppm) / Atualmente, a utiliza??o de produtos qu?micos que atendam satisfatoriamente
as necessidades de diferentes setores da ind?stria qu?mica encontra-se
vinculada ao consumo de materiais biodegrad?veis. Neste contexto, o presente
trabalho foi desenvolvido contemplando aspectos biotecnol?gicos com o
objetivo de se desenvolver um inibidor de corros?o menos agressivo ao meio
ambiente. Para tanto, uma nanoemuls?o (denominada de NE-OS) foi obtida
com Tween 80 (polioxietileno (20) monooleato), ?leo de soja (OS) e ?gua
bidestilada. A modifica??o dos percentuais deste tensoativo sorbitano (entre 9
e 85 ppm) foi avaliada em diagramas de fases em que se manteve constante o
percentual da fase ?leo, possibilitando a forma??o do sistema NE-OS em
diferentes concentra??es. Desta forma, nanoemuls?es (NE-OS1, S2, S3, S4 e
S5) polares (do tipo O/A) foram caracterizadas (an?lise de dispers?o de luz,
condutividade e pH) e submetidas a estudos eletroqu?micos. O comportamento
interfacial destes sistemas nanoemulsionados como inibidores de corros?o na
presen?a de a?o-carbono AISI 1020, em meio salino (NaCl 3,5%) foi avaliado
pela determina??o do Potencial de Circuito Aberto (OCP), Curvas de
Polariza??o (obtidas pela extrapola??o das curvas de Tafel) e Espectroscopia
de Imped?ncia Eletroqu?mica (EIE). De acordo com os resultados obtidos pelas
an?lises das Curvas de Polariza??o, foi poss?vel caracterizar o sistema NE-OS
(e suas varia??es) como inibidores mistos com efici?ncias m?ximas de
inibi??es quantitativas (98,6% - 99,7%) para NE-OS1 e NE-OS2 (9 - 85 ppm do
tensoativo). No entanto, de acordo com a t?cnica EIE, as efici?ncias m?ximas
de inibi??es quantitativas foram observadas para v?rias amostras deste
sistema NE-OS. Como ferramentas adicionais aos estudos eletroqu?micos
foram realizados quimiom?tricos de An?lise de Vari?ncia (ANOVA) e An?lise de
Componentes Principais (PCA), utilizadas, respectivamente, para
caracteriza??o das nanoemuls?es e estudo de isotermas de adsor??o, que
confirmaram os resultados observados nas investiga??es experimentais em
que se utilizaram as nanoemuls?es dilu?das com o tensoativo em
concentra??es reduzidas (0,5 1,75 ppm)
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/17700 |
| Date | 30 August 2012 |
| Creators | Rodrigues, Ciro Jos? Ferreira |
| Contributors | CPF:37320165449, http://lattes.cnpq.br/5360188002708095, Gurgel, Alexandre, CPF:59721421472, http://lattes.cnpq.br/5266735277153768, Rossi, C?tia Guaraciara Fernandes Teixeira, CPF:77044568491, http://lattes.cnpq.br/0103853142184734, Lima, K?ssio Michell Gomes de, CPF:03144855464, http://lattes.cnpq.br/6928918856031880, Maciel, Maria Aparecida Medeiros |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Qu?mica, UFRN, BR, F?sico-Qu?mica; Qu?mica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds