There are many examples where creation and usage of porous substrates
play important roles in various fields of application in material science and
technology. In the manufacture of ceramic products, as an alternative to the plaster molds, porous resin molds are used in order to resolve the drawbacks that result A porous substrate can be produced by various ways. In this study, porous polymeric matrices of poly(methyl methacrylate) (PMMA) and poly(methyl methacrylate-co-2-hydroxyethyl methacrylate) [poly(MMA-HEMA)] polymers were prepared by connecting the polymer microspheres to each other by an epoxy adhesive. To improve the surface properties, methyl methacrylate (MMA) was copolymerized with 2-hydroxyethyl methacrylate (HEMA). The microspheres used were synthesized by suspension polymerization and characterization was
done by Nuclear Magnetic Resonance (NMR), Particle Size Analyzer and
Scanning Electron Microscope (SEM). The porous samples were prepared with
PMMA and poly(MMA-HEMA) copolymer microspheres with two different HEMA contents and their surface energies were measured. In addition, the effect of mean particle diameter of the microspheres used and the epoxy content of the solution used to bind the microspheres, on the impregnation capacity, morphology
and the impact strength of the porous samples prepared, were studied.
Inclusion of HEMA into the formulation improved the impregnation capacity of the samples. Using microspheres with narrower particle size distribution resulted in larger representative capillary radii and higher rate of impregnation of the samples. Increasing the epoxy content of the solution used to bind the beads, increased the impact strengths of the samples prepared.
Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/4/1045343/index.pdf |
Date | 01 January 2003 |
Creators | Agirtopcu, Yasin |
Contributors | Bayramli, Erdal |
Publisher | METU |
Source Sets | Middle East Technical Univ. |
Language | English |
Detected Language | English |
Type | M.S. Thesis |
Format | text/pdf |
Rights | To liberate the content for public access |
Page generated in 0.0022 seconds