The diploma thesis deals with selected fracture tests and evaluation of fracture parameters of cement-based composite. One part of the thesis deals with cement-based composite with glass spherical aggregate of a single fraction of 2 mm. After production, the beams with dimensions of 20×40×200mm exposed to temperatures in the range from 100 to 1000 °C for one hour. Using the non-destructive ultrasonic pulse method, the degree of damage caused by termal load was determined. Selected specimen with central edge notch were then tested in three-point bending and fragments after these tests were tested in compression. In the second part, attention was paid to the evaluation of fracture tests conducted on specimen from drill-cores taken from selected objects located at the former Transgas Gas Control Center in Prague. The specimen were provided with a chevron notch before being tested in three-point bending. The measured data was modified by the GTDiPS program and in the case of the glass composite the StiCrack program was used to evaluate fracture parameters.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:392121 |
| Date | January 2019 |
| Creators | Majda, Tomáš |
| Contributors | Malíková, Lucie, Keršner, Zbyněk |
| Publisher | Vysoké učení technické v Brně. Fakulta stavební |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds