Previous issue date: 2015-07-02 / Neste trabalho foi feito um estudo das propriedades estruturais e magnéticas de filmes granulares de cromita de cobalto sobre substrato de silicio. Aqui os filmes foram fabricados a partir do método químico sol‐gel, técnica de centrifugação spincoating e
Tratamento térmico apropriado. Toda família de filmes foi fabricada sobre substrato de silício (100) e submetida a tratamento termico. A diferença de um filme para outro esta na quantidade de material depositado. Isto possibilitou o estudo das propriedades supracitadas em função da quantidade de material depositado para fabricação do filme. A cristalinidade de todas as amostras obtidas foi confirmada por difração de raios-X (XRD). A microscopia eletrônica de varredura (MEV) mostrou filmes granulares com boa homogeneidade e que a espessura de todas as amostras aumenta com a quantidade de gotas depositadas durante o spin‐coating. As propriedades magnéticas foram medidas usando magnetometria de amostra vibrante (VSM). O campo aplicado durante a medicao foi orientado paralelo ao plano do filme e observou‐se uma alta coercividade e que esta diminui quase linearmente com o aumento de temperatura. / In this work we have made a study of the structural and magnetic properties of cobalt chromite granular films over silicon substrate. Here the films were fabricated by the chemical method sol‐gel, spin coating technique and ppropriate heat treatment. The entire Family was deposited over silicon substrate (100) and submitted to heat treatment. The difference between a film to another is the quantity of deposited
Material. This allowed the study of the above properties as a function of the deposited material. The crystallinity of all samples obtained was confirmed by X‐ray diffraction (XRD). The scanning electron microscopy (SEM) showed granular films with good homogeneity and the thickness of all samples increases when the number of drops increases during spin‐coating. The magnetic properties were measured using vibrating sample magnetometry (VSM). The applied field during the measurement was
Oriented parallel to the film plane and observed a high coercivity and that decreases pproximately linearly with increasing temperature.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/20045 |
| Date | 02 July 2015 |
| Creators | FARIAS, Bruno Veríssimo de Miranda |
| Contributors | http://lattes.cnpq.br/3590036930228473, HERNANDEZ, Eduardo Padrón |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Ciencia de Materiais, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Breton |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds