A process for the production of clean hydrogen from methane based upon the sequential reduction and oxidation of metal oxides has been studied. The original process, based on iron oxide, suffers from significant disadvantages including deactivation by sintering and coke deposition. Improvement of the iron based system and identification and development of alternative metal oxides for hydrogen production has formed the basis of this study. The literature review outlines current methods for hydrogen production, followed by a review of the Steam-Iron Process as an improved and simpler method for clean hydrogen production. Thermodynamic assessment shows Fe3O4/FeO/Fe, WO3/WO2/W and SnO2/SnO/Sn to be the most prospective systems for the Steam-Metal Process. Experimental testing showed that Fe and W based systems were suitable for hydrogen production, but Sn based systems were unsuitable due to poor reducibility using methane. Attention was then focused on the addition of CeO2/ZrO2 promoters to Fe and W based systems in order to improve reactivity and prevent catalyst deactivation. CeO2/ZrO2 promoted Fe2O3 showed improved redox reactivity and increased stability, with formation of FeO. This aided in mitigation of sintering and introduced the possibility of prevention of coking, as catalysed by methane decomposition over fully reduced Fe metal. Although WO3 was found to be a suitable oxide, complete reduction to tungsten metal resulted in the formation of tungsten carbide and contamination of hydrogen produced. The formation of 31mol% [CeO2/ZrO2] / 69 mol% WO3 showed stabilised reduction using methane, allowing for redox cycling of the WO3-WO2 couple and preventing complete reduction to W metal. The use of the doped metal oxide showed the best performance of all the metal oxides tested, with clean hydrogen production over multiple redox cycles and high metal oxide stability. Further kinetic studies of both the reduction and oxidation reactions show reduction is chemical reaction controlled process (WO3/WO2.9 → WO2) with an apparent activation energy of 142 ?? 3 kJ/mol. Oxidation is also fitted to a chemically controlled process, with a reaction rate expression derived as: rH2 = [0.064 + (F x 0.00038)].e^(-108750/8.314xT).[PH2O]^(0.75) The apparent activation energy for oxidation was calculated as 109 ?? 1 kJ/mol.
| Identifer | oai:union.ndltd.org:ADTP/282217 |
| Date | January 2010 |
| Creators | Sim, Andrew Gregory, Chemical Sciences & Engineering, Faculty of Engineering, UNSW |
| Publisher | Awarded By:University of New South Wales. Chemical Sciences & Engineering |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0074 seconds