Orientador: Roseana da Exaltação Trevisan / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia mecanica / Made available in DSpace on 2018-08-04T08:55:23Z (GMT). No. of bitstreams: 1
Silva_JoseHiltonFerreirada_D.pdf: 14751352 bytes, checksum: 7fbb40ac7c73c18bb5c602fe3a79f20d (MD5)
Previous issue date: 2005 / Resumo: Este trabalho tem como objetivo principal propor um novo ensaio para avaliar a susceptibilidade de metais de solda ao fenômeno de trincas induzidas pelo hidrogênio em diferentes ambientes. O novo ensaio é composto de duas propostas: a primeira consiste em viabilizar a aplicação do teste G-BOP (Gapped Bead-On-Plate) em chapas finas: a espessura do corpo de prova (50,8mm) é obtida através da montagem de blocos conjugados com chapas finas
do aço avaliado como metal de base e chapas de aço ABNT 1020; a segunda proposta baseia-se numa metodologia para realizar os ensaios do teste G-BOP em um ambiente saturado com H2S. Para o desenvolvimento do trabalho foi usado o processo de soldagem a arco com eletrodo tubular (FCAW). Os parâmetros de controle utilizados foram a energia nominal de soldagem e a constante de deposição. O desenvolvimento experimental foi realizado de forma totalmente aleatória, com o auxílio de um procedimento conhecido como planejamento fatorial (PF); foram utilizadas como variáveis de influência o tipo de arame tubular, a temperatura de preaquecimento e o ambiente de ensaio. Como variável de resposta foi avaliado o percentual de trincas de hidrogênio (TH)presente no metal de solda do aço API X80. Os resultados foram submetidos à análise de variância e validados para uma confiança de 90%. Os resultados de trincas de hidrogênio foram discutidos em função da composição química, microestrutura, modos de fraturas e hidrogênio residual do metal de solda. Concluiu-se que a nova proposta de teste G-BOP modificado foi eficaz na avaliação da sensibilidade dos metais de solda ao trincamento induzido pelo hidrogênio; a exposição ao H2S fragilizou os metais de solda executados à temperatura ambiente e aumentou a susceptibilidade dos arames tubulares às trincas de hidrogênio. Ainda como resultados deste trabalho pode-se concluir que o preaquecimento do aço API X80 evitou o trincamento do metal de solda e que os arames tubulares mostraram-se susceptíveis ao trincamento por hidrogênio quando soldados à temperatura ambiente / Abstract: The main objective ofthis work is to propose a new test to evaluate the susceptibility of weld metaIs to the phenomenon ofhydrogen induced cracking in different environrnents. The new test is a combination oftwo procedures: the first is to make possible the application of GBOP (Gapped Bead-on-Plate) test on steel sheets. The thickness ofthe workpiece (2 inches) is gotten through the sandwich assembly with steel sheets of the evaluated steel as weld metal and ABNT 1020 steel; the second is to carry out the G-BOP tests in a H2Ssaturated environrnent. The tests were perfonned with the Flux Cored Arc Welding process (FCAW). Welding energy and the deposition were kept constant during the tests. The experimental were carried out with a random factorial designoThe input variables were cored wire kind, preheat temperature and environrnent testoThe hydrogen cracking percentage in weld metal of API X80 steel was the output variable. Results were submitted to a variance analysis and a 90% confidence interval was utilized. The results of cold cracking were discussed in function ofthe chemical composition, microstructure, fracture mode and trapped hydrogen in weld metal. It can be concludedthat the new modified GBOP test proposed was powerful in the evaluation of the sensitivity ofweld metaIs to the hydrogen induced cracking; the H2S rich environrnent brittled the weld metal executed at room temperature and increased the susceptibility ofthe cored wires to hydrogen induced cracking. Furthermore, the preheat temperature of API X80 steel avoided the cold cracking in weld metal and, the cored wires showed susceptibility to hydrogen cracking when welded at room temperature / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263156 |
| Date | 24 February 2005 |
| Creators | Silva, Jose Hilton Ferreira da |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Trevisan, Roseana da Exaltação, 1951-, Diniz, Anselmo Eduardo, 1959-, Button, Sergio Tomini, Ferraresi, Valtair Antonio, Machado, Ivan Guerra |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 158p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds