by Cheng Kai. / Thesis (M.Phil.)--Chinese University of Hong Kong, 1997. / Includes bibliographical references. / by Cheng Kai. / Acknowledgments --- p.i / Abstract --- p.ii / Table of content --- p.iv / Chapter Chapter One --- Introduction / Chapter 1.1 --- Barkhausen emission --- p.1 / Chapter 1.2 --- Methods of measurements --- p.3 / Chapter 1.2.1 --- Magnetization of a sample --- p.4 / Chapter 1.2.2 --- Signal detection --- p.5 / Chapter 1.2.3 --- Signal processing --- p.5 / Chapter 1.3 --- Instrumentation --- p.6 / Chapter 1.3.1 --- Instron loading machine --- p.6 / Chapter 1.3.2 --- Optical microscopy --- p.7 / Chapter 1.3.3 --- Vicker's hardness tester --- p.7 / Chapter 1.3.4 --- Ceramic furnace --- p.8 / References --- p.9 / Chapter Chapter Two --- Domain Theory / Chapter 2.1 --- The postulate of domain --- p.16 / Chapter 2.2 --- Domain energy --- p.18 / Chapter 2.3 --- The magnetization process --- p.20 / Chapter 2.4 --- Effect of applied stress --- p.22 / Chapter 2.5 --- Hindrances to wall motion by inclusions --- p.23 / References --- p.24 / Chapter Chapter Three --- Steels / Chapter 3.1 --- The making of steel --- p.28 / Chapter 3.2 --- The iron-iron carbide phase diagram --- p.29 / Chapter 3.3 --- Heat treatment of plain-carbon steels --- p.29 / Chapter 3.3.1 --- Slow cooling of plain-carbon steels --- p.29 / Chapter 3.3.2 --- Rapid cooling of plain-carbon steels --- p.30 / Chapter 3.3.3 --- Annealing --- p.31 / References --- p.32 / Chapter Chapter Four --- Effects of carbon on Barkhausen emission in plain carbon steel / Chapter 4.1 --- introduction --- p.35 / Chapter 4.2 --- Experiments --- p.36 / Chapter 4.2.1 --- Samples --- p.36 / Chapter 4.3 --- Results and discussions --- p.37 / Chapter 4.4 --- Conclusions --- p.39 / References --- p.40 / Chapter Chapter Five --- Magnetization process in a steel plate/bar subjected to an increasing tensile load / Chapter 5.1 --- Introduction --- p.45 / Chapter 5.2 --- Experiments --- p.47 / Chapter 5.3 --- Results and discussions for the zinc-coated steel plate --- p.47 / Chapter 5.4 --- Results and discussions for mild steel --- p.50 / Chapter 5.5 --- A comparison between steel plate and steel bar --- p.52 / Chapter 5.6 --- Conclusions --- p.53 / References --- p.54 / Chapter Chapter Six --- Evaluation of residual stress in bent steel bars subjected to different heat treatment by Barkhausen emission / Chapter 6.1 --- Introduction --- p.60 / Chapter 6.2 --- Experiments --- p.60 / Chapter 6.3 --- Results and discussions --- p.61 / Chapter 6.4 --- Conclusions --- p.64 / References --- p.65 / Chapter Chapter Seven --- Effects of heat treatment on electrolytic zinc-coated steel plates by Barkhausen emission / Chapter 7.1 --- Introduction --- p.72 / Chapter 7.2 --- Experiments --- p.72 / Chapter 7.3 --- Results and discussions --- p.73 / Chapter 7.4 --- Conclusions --- p.75 / References --- p.76 / Chapter Chapter Eight --- Effects of demagnetizing and stray fields on Barkhausen emission / Chapter 8.1 --- Introduction --- p.80 / Chapter 8.2 --- Experiments --- p.80 / Chapter 8.3 --- Results and discussions --- p.81 / Chapter 8.4 --- Conclusions --- p.85 / References --- p.85 / Chapter Chapter Nine --- Conclusions and suggestions for further studies --- p.90
Identifer | oai:union.ndltd.org:cuhk.edu.hk/oai:cuhk-dr:cuhk_321996 |
Date | January 1997 |
Contributors | Cheng, Kai., Chinese University of Hong Kong Graduate School. Division of Physics. |
Source Sets | The Chinese University of Hong Kong |
Language | English |
Detected Language | English |
Type | Text, bibliography |
Format | print, vi, 93 leaves : ill. ; 30 cm. |
Rights | Use of this resource is governed by the terms and conditions of the Creative Commons “Attribution-NonCommercial-NoDerivatives 4.0 International” License (http://creativecommons.org/licenses/by-nc-nd/4.0/) |
Page generated in 0.0019 seconds