Engineered wood products (EWP) are becoming extremely popular and a viable material option for the construction of residential, commercial, and hybrid buildings. Cross-laminated timber (CLT) is among one of the many EWP available in North America, which can be utilized for many different applications such as: walls, floors, and roofs. Despite the available requirements in the Canadian blast design standard (CSA, 2012) with regard to the design of wood structures, there are currently no provisions on how to retrofit timber structures to improve their performance when subjected to blast loads. The current study is aimed at investigating the effect of different retrofitting alternatives in order to improve the overall behaviour of CLT when exposed to out-of-plane bending.
The experimental program examined the behaviour of seventeen reinforced CLT slabs. Testing was conducted at the University of Ottawa by means of a shock tube capable of simulating high strain rates similar to those experienced during a blast event. The current study was divided into two phases. The first consisted of CLT slabs retrofitted with steel straps where strap spacing, location, and order of installation was investigated. The second phase focused on the development of dynamic properties of CLT panels when reinforced with GFRP. Lay-up configuration and fabric orientation were among the parameters explored.
The results from the experimental program show that reinforcing the panels with steel straps had minimal effect on the ultimate strength, but significant levels of post peak resistance and ductility was achieved. The horizontal straps were able to restrict the failure to small regions and to promote flexural failure by preventing rolling shear failure. It also eliminated flying debris and enhanced the ultimate strength, stiffness as well as ductility. Applying GFRP layers enhanced the overall behaviour of the slab resulting in a significant increase in peak resistance, ductility, and stiffness when compared to the dynamic results of an unretrofitted panel. The post peak resistance was also greatly improved. In particular, applying stacked quadraxial lay-up configuration significantly improved the ductility and resulted in the greatest post peak resistance. The effect of steel straps on damaged and retrofitted was relatively minimal, and only partial recovery of the resistance and the stiffness was achieved. GFRP with full confinement yielded better performance compared to the unretrofitted and undamaged counterpart. More work is needed to quantify the benefits of using GFRP in these applications.
| Identifer | oai:union.ndltd.org:uottawa.ca/oai:ruor.uottawa.ca:10393/38247 |
| Date | 09 October 2018 |
| Creators | Lopez-Molina, America Maria |
| Contributors | Doudak, Ghasan |
| Publisher | Université d'Ottawa / University of Ottawa |
| Source Sets | Université d’Ottawa |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf |
Page generated in 0.0023 seconds