Joining two dissimilar metals, specifically Mg and Al alloys, using conventional welding techniques is extraordinarily challenging. Even when these alloys are able to be joined, the weld is littered with defects such as cracks, cavities, and wormholes. The focus of this project was to use friction stir welding to create a defect-free joint between Al 2139 and Mg WE43. The stir tool used in this project, made of H13 tool steel, is of fixed design. The design included an 11 mm scrolled and concave shoulder in addition to a 6 mm length pin comprised of two tapering, threaded re-entrant flutes that promoted and amplified material flow. Upon completion of this project an improved experimental setup process was created as well as successful welds between the two alloys. These successful joints, albeit containing defects, lead to the conclusion that the tool used in project was ill fit to join the Al and Mg alloy plates. This was primarily due to its conical shaped pin instead of the more traditional cylindrical shaped pins. As a result of this aggressive pin design, there was a lack of heat generation towards the bottom of the pin even at higher (800-1000 rpm) rotation speeds. This lack of heat generation prohibited the material from reaching plastic deformation thus preventing the needed material flow to form the defect free joint.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc955097 |
| Date | 12 1900 |
| Creators | Reese, Gregory A |
| Contributors | Fortier, Aleksandra, Horne, Kyle, Li, Xiaohua |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Reese, Gregory A, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0016 seconds