Nanoindentation has brought in many features of research over the past decade. This novel technique is capable of producing insights into the small ranges of deformation. This special point has brought a lot of focus in understanding the deformation behavior under the indenter. Nickel, iron, tungsten and copper-niobium alloy system were considered for a surface deformation study. All the samples exhibited a spectrum of residual deformation. The change in behavior with indentation and the materials responses to deformation at low and high loads is addressed in this study. A study on indenter geometry, which has a huge influence on the contact area and subsequently the hardness and modulus value, has been attempted. Deformation mechanisms that govern the plastic flow in materials at low loads of indentation and their sensitivity to the rate of strain imparted has been studied. A transition to elastic, plastic kind of a tendency to an elasto-plastic tendency was seen with an increase in the strain rate. All samples exhibited the same kind of behavior and a special focus is drawn in comparing the FCC nickel with BCC tungsten and iron where the persistence of the elastic, plastic response was addressed. However there is no absolute reason for the inconsistencies in the mechanical properties observed in preliminary testing, more insights can be provided with advanced microscopy techniques where the study can be focused more to understand the deformation behavior under the indenter. These experiments demonstrate that there is a wealth of information in the initial stages of indentation and has led to much more insights into the incipient stages of plasticity.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc4904 |
| Date | 12 1900 |
| Creators | Vadlakonda, Suman |
| Contributors | Mirshams, Reza, Banerjee, Rajarshi, Kaufman, Michael |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Copyright, Vadlakonda, Suman, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0155 seconds