The main objective of this work is to propose a mechanism for the transfer of impurities into the
sucrose crystal. To this end the transfer of impurities into the sucrose crystal was investigated,
under crystallisation conditions similar to those found industrially. Most of the impurities, namely,
colour bodies, potassium, calcium and starch, were selected on the basis of their industrial
importance, but some exotic species, namely lithium and nickel, were chosen to represent other
mono- and di-valent ions respectively, and dyes, such as methylene blue, which have been used
in work with single crystal sucrose crystallisation, were included to make the results more general.
A parameter to measure the rate at which impurities are transferred into the sucrose crystal was
proposed. Experiments, carried out in a pilot plant evaporative crystalliser, were performed to
establish the effect of selected factors on both the concentrations of impurities found in the
sucrose crystal, and on the rate at which these impurities are incorporated into the crystal. All the
factors selected, namely the rate of crystallisation, the temperature, the concentration and type
of impurity, the diffusivity of the impurity in concentrated sucrose solutions, and the crystal
dimensions, are shown to influence the rate of impurity transfer. Only the concentration in the
feed and type of impurity, however, affect the final concentration of the impurity in the crystal.
Concepts involving partition coefficients and adsorption isotherms were also investigated. The
experimental data did not fit the adsorption isotherm models well, but the values obtained for the
partition coefficients were similar to those quoted in the literature when exchange types of
reactions are operative. Activation energies have been measured, both for the rate of crystallisation of sucrose, and for
the rates of impurity transfer. The values obtained, particularly for the rate of impurity transfer, indicate that a transport mechanism is effective. The experimental results have been used to investigate the relevance of two models, one
involving a two-step approach and the other an interfacial process, for the incorporation of the impurity into the sucrose crystal. The results obtained indicate that the interfacial breakdown model describes the transfer of all the impurities studied here, except for starch. / Thesis (Ph.D.)-University of Natal, Durban, 1998.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:ukzn/oai:http://researchspace.ukzn.ac.za:10413/8602 |
Date | January 1998 |
Creators | Lionnet, Georges Raoul Edouard. |
Contributors | Martincigh, Bice S., Purchase, Brian. |
Source Sets | South African National ETD Portal |
Language | en_ZA |
Detected Language | English |
Type | Thesis |
Page generated in 0.3078 seconds