This thesis is focused on the possibilities of the utilization of the fludized fly ash in ceramic technology, especially in the field of brick manufacturing and ceramic tiles. There were used fly ashes from thermal power plants in Hodonín, Ledvice and Tisová. Fluidized fly ash can be used for manufacturing of building materials. There hasn’t been done extensive research in this area. One of the problem is sulphur dioxide leakage during burning. The work describes the behaviour of fluidized ash during firing. The attention is focused on air pollution of sulphur dioxide. The production of SO2 is controlled so that the aim of the work is to find a way how to avoid leaking. It was proved that addition of sodium ions causes the formation of minerals hauyne and nosean during firing. Also is described the behaviour of the fly ash-soil mixtures. The anhydrite decomposition temperature is lower than in pure fly ash. In the end is fluidized ash applied for the production of dry pressed ceramic tiles. This ash can be used in ceramic technology. However, despite the interesting results there are number of problems that need to be solved.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:355609 |
| Creators | Keršnerová, Lucie |
| Contributors | Šveda,, Mikuláš, Rovnaníková, Pavla, Všianský,, Dalibor, Sokolář, Radomír |
| Publisher | Vysoké učení technické v Brně. Fakulta stavební |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds