Oxidation Resistance and Nanoscale Oxidation Mechanisms in Model Binary and Ternary Alloys Exposed to Supercritical Water

The oxidation behavior of model binary and ternary alloys in supercritical water (SCW) was examined. Binary alloys contained 9 or 14 at% Cr. Ternary alloys had 1.5 at% of one of the following elements: Si, Al, V, Mn or Ti. Samples with different surface finishes were exposed to SCW for up to 500 hours. The oxidized samples were characterized using gravimetry, SEM, HRTEM and EDX. After exposure, a uniform double layer oxide with outwardly grown magnetite inwardly grown Fe-Cr mixed oxide was detected on most of samples. Alloys contains 14 at% Cr or/and 1.5 at% Si showed a mixed oxidation mode, where relatively thick double layer oxides coexisted with thin protective oxide. The coverage with the thin oxide increased with the increase of deformation and/or Cr and/or Si content. A 20 nm thick Si-enriched layer was detected at such alloy/oxide interfaces. This behavior is very similar to “third element effect”.

Identiferoai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/33288
Date20 November 2012
CreatorsLi, Weimi
ContributorsNewman, Roger C.
Source SetsLibrary and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada
Languageen_ca
Detected LanguageEnglish
TypeThesis

Page generated in 0.0021 seconds