Non-equilibrium plasma modification of polymer surfaces in an oxygen atmosphere provides a highly efficient, solventless method of raising the surface energy. The chemical and physical effects of non-equilibrium plasma treatment on polymer surfaces have been investigated. Oxygen glow discharge and silent discharge treatment of several polymers (polypropylene, polystyrene, polyphenylene oxide and polycarbonate) has been shown to cause both surface oxidation and chain scission at the polymer surface. This generates low molecular weight oxidised material on the polymer surface which conglomerates into globular features due to the difference in surface energy between the oxidised material and the untreated polymer. These features can be removed by solvent washing. Generally silent discharge treatment generates more low molecular weight oxidised material whereas oxygen glow discharge treatment generates more non-soluble oxidised material. Crystalline polymers react at a slower rate than amorphous material. During the treatment of a model crystalline polymer (hexatriacontane) the plasma attacks the edges of the crystal, rather than the surface, due to the greater chain mobility at the edge. Non-equilibrium plasma treatment of both miscible and immiscible polymer blends were investigated. The size and distribution of the globular features formed were found to be dependent on the blend composition. For the immicible polymer blend, non-equilibrium plasma treatment reveals the blend morphology mi sing from the difference in reaction rates of the parent polymers.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:336318 |
| Date | January 1996 |
| Creators | Boyd, Robert Deric |
| Publisher | Durham University |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://etheses.dur.ac.uk/5180/ |
Page generated in 0.0022 seconds