Efeitos da usinagem na integridade superficial de um aço inoxidavel superaustenitico / Effects of the machining in the surface integrity on the superaustenitic stainless steel

Orientadores: Paulo Roberto Mei, Anselmo Eduardo Diniz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-12T19:31:21Z (GMT). No. of bitstreams: 1
Gravalos_MarcioTadeu_M.pdf: 4613359 bytes, checksum: 86f814729e45d2e34702f6735566c398 (MD5)
Previous issue date: 2008 / Resumo: Foram investigados os efeitos das condições de usinagem em operação de torneamento na integridade superficial do aço inoxidável superaustenítico ASTM A744 Gr.CN3MN. A operação de acabamento foi o foco principal, porém também foram realizados estudos com a operação prévia, de desbaste. As principais variáveis no acabamento foram: ângulo de saída da ferramenta, velocidade de corte, profundidade de corte e avanço. No desbaste variou-se somente o ângulo de saída e a velocidade de corte. Os ensaios foram realizados em um torno horizontal CNC, utilizando fluido de corte. Os parâmetros analisados foram: microestrutura por microscopia ótica, rugosidade, encruamento por ensaio de microdureza e tensão residual por difração de raio-X. Para se estudar a resistência à corrosão por pites, superfícies usinadas foram imersas em solução de cloreto de ferro e examinadas no estereoscópio, medindo-se, por área, a densidade de pites e a perda de massa. Os resultados mostraram a presença de tensão residual de tração e de uma camada encruada em todas as superfícies usinadas. A redução da rugosidade elevou a resistência à corrosão por pite. A melhor combinação das condições de corte encontrada para obter os menores valores de rugosidade e de tensão residual de tração, no acabamento, para profundidade de corte de 0,2 ou 0,4 mm, foi a maior velocidade de corte (120 m/min), o menor avanço (0,1 mm/rot) e o maior ângulo de saída (10º), no desbaste; para a profundidade de corte de 2,5 mm e avanço de 0,25 mm/rot., foi a menor velocidade de corte (60 m/min) e o maior ângulo de saída (10º). / Abstract: An investigation was made of the effects of the machining conditions employed in the turning operation on the surface integrity of ASTM A744 Grade CN3MN superaustenitic stainless steel. The main focus was the finishing operation, but studies were also carried out with a prior roughening operation. The main input variables in finishing were: tool rake angle, cutting speed, cutting depth and feed rate. The only input variables in the roughening operation were rake angle and cutting speed. The tests were conducted on a CNC horizontal lathe, using cutting fluid flood. The following parameters were analyzed: microstructure and roughness - examined by optical microscopy; work hardening - determined by microhardness measurements; and residual stress - analyzed by X-ray diffraction. To study the pitting corrosion resistance, machined surfaces were immersed in a ferric chloride solution and examined under a stereoscope, measuring the pits density and mass loss per area. The results revealed the presence of residual tensile stress and a hardened layer on all the machined surfaces. Reducing the roughness caused the pitting corrosion resistance to increase. To obtain the lowest values of roughness and residual tensile stress in finishing at cutting depths of 0.2 or 0.4 mm, the best combination of cutting conditions was the highest cutting speed (120 m/min), the lowest feed rate (0.1 mm/v), and the highest rake angle (10º). In roughening at a cutting depth of 2.5 mm and a feed rate of 0.25 mm/rot., the best combination was the lowest cutting speed (60 m/min) and the highest rake
angle (10º). / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263125
Date12 October 2008
CreatorsGravalos, Marcio Tadeu
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Diniz, Anselmo Eduardo, 1959-, Mei, Paulo Roberto, 1953-, Hassui, Amauri, Martins, Marcelo
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format118p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0027 seconds