A special wafer bonding method called the Silicon Direct Bonding technique is used to study the bonding of unipolar (n-type, <100> oriented) silicon wafers. The primary objective of this thesis project is to find an optimum surface preparation technique for subsequent silicon wafer bonding. Wafer cleaning and treatment methods are investigated to understand the correlation between a high quality wafer surface and the resulting high quality electrical conduction at the interface. Accordingly, in this project, a preference for hydrophobic (less polar Si-OH surface) wafers is given to ensure a minimized amount of oxide layer on the surface. Several key factors that govern the quality of the wafer surfaces, such as the degree of hydrophobicity, HF etching time, composition of HF etching solution and Dr water rinse, are examined with ellipsometric and XPS measurements. An HF etching followed by a sputter etching has been selected to pre-treat the wafer surfaces for bonding. A maximum allowable air exposure time (35 second) is also found which would allow bonding without significant re-growth of the oxide layer. Bonding is performed under vacuum with a special mechanical fixture and the resulting structures from a subsequent heat treatment process are examined with crack propagation testing. Bond strength after annealing is sufficient to withstand a pull test, however, with a 3 point bend testing, the crack propagated horizontally at the interface. / Master of Science
Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/41520 |
Date | 12 March 2009 |
Creators | Haque, Ashim Shatil |
Contributors | Electrical Engineering, Moore, Daniel J., Elshabini-Riad, Aicha A., Desu, Seshu B. |
Publisher | Virginia Tech |
Source Sets | Virginia Tech Theses and Dissertation |
Language | English |
Detected Language | English |
Type | Thesis, Text |
Format | viii, 80 leaves, BTD, application/pdf, application/pdf |
Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Relation | OCLC# 30114364, LD5655.V855_1993.H372.pdf |
Page generated in 0.0025 seconds