Magnesium and its alloys have been considered for load-bearing implant materials due to their similar mechanical properties to the natural bone, excellent biocompatibility, good bioactivity, and biodegradation. Nevertheless, the uncontrollable corrosion rate in biological environment restrains their application. Hydroxyapatite (HA, Ca10(PO4)6(OH)2) is a widely used bio-ceramic which has bone-like mineral structure for bone fixation. Poor fracture toughness of HA makes it not suitable for load-bearing application as a bulk. Thus, HA is introduced into metallic surface in various forms for improving biocompatibility. Recently friction stir processing (FSP) has emerged as a surface modification tool for surface/substrate grain refinement and homogenization of microstructure in biomaterial. In the pressent efforts, Mg-nHA composite surface on with 5-20 wt% HA on Mg substrate were fabricated by FSP for biodegradation and bioactivity study. The results of electrochemical measurement indicated that lower amount (~5% wt%) of Ca in Mg matrix can enhance surface localized corrosion resistance. The effects of microstructure,the presence of HA particle and Mg-Ca intermetallic phase precipitates on in vitro behavior of Mg alloy were investigated by TEM, SEM, EDX,XRD ,and XPS. The detailed observations will be discussed during presentation.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc862762 |
| Date | 08 1900 |
| Creators | Ho, Yee Hsien |
| Contributors | Dahotre, Narendra B., Mukherjee, Sundeep, Banerjee, Raj, Du, Jincheng, Zhao, Weihuan |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Ho, Yee Hsien, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0024 seconds