From many years YSZ is used as the top coat material for TBC's, as it has good phase stability up to 1200°C, higher fracture toughness, lower thermal conductivity, erosion resistance & higher coefficient of thermal expansion. But, it has a drawbacks at high temperature such as sintering and transformation of phases. For this reason new ceramic materials with pyrochlores crystal structure such as Gd2Zr2O7 are being considered as it has high melting points, phase stability, lower thermal conductivity and CMAS resistance. But it has low fracture toughness when compared to YSZ. In order to take advantage of low thermal conductivity and high thermal stability of gadolinium zirconate and avoiding the drawbacks of low coefficient of thermal expansion and low toughness using YSZ, a double/multi-layer coatings approach is being used. Therefore, multi-layer TBCs are sprayed and compared with single layer coating in this work. These coatings are processed by suspension plasma spraying. For single layer coating YSZ is used, for double layer coating YSZ as the intermediate coating and Gd2Zr2O7 as the top coat is used. Additionally, a triple layer coating system comprising YSZ, Gd2Zr2O7 and dense Gd2Zr2O7 as top coat is also sprayed. The as sprayed coatings are characterized for microstructure analysis using optical microscope and scanning electron microscope (SEM), elemental analysis of TGO using Energy-Dispersive Spectrometer (EDS). XRD analysis was done to identify various phases in the coating. Porosity analysis using Archimedes principle was carried out. Thermal cyclic fatigue (TCF) test of the sprayed coatings was carried out at 1100°C. Failure analysis of the TCF specimens was carried out using SEM/EDS. TCF results showed that the triple layer coatings (dense Gd2Zr2O7/Gd2Zr2O7/YSZ) had higher thermal cyclic fatigue life and lower TGO thickness when compared to single layer (YSZ) and double layer (Gd2Zr2O7/YSZ) TBCs.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hv-8266 |
| Date | January 2015 |
| Creators | Gokavarapu, Naga Sai Pavan Rahul |
| Publisher | Högskolan Väst, Avd för tillverkningsprocesser |
| Source Sets | DiVA Archive at Upsalla University |
| Language | Swedish |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds