Avaliação longitudinal da resistência de união de pinos de fibra de vidro à dentina cimentados com quatro agentes cimentantes por meio do teste de push-out

Avaliou-se a resistência de união do pino de fibra de vidro à dentina cimentado com quatro agentes cimentantes, por meio do teste push-out realizado após 24 horas e seis meses de armazenagem. Foram selecionados 80 dentes humanos uniradiculares, tratados endodonticamente e divididos aleatoriamente em quatro grupos (n=20), variando-se o tipo de cimento utilizado: grupo I: cimento de ionômero de vidro reforçado com resina (Fuji PlusTM, GC Corp., Tokyo, Japan); grupo II: cimento resinoso usando sistema adesivo convencional de 3 passos de aplicação (RelyX ARC + Scotchbond Multi-purpose, 3M ESPE, St Paul, MN, USA); grupo III: cimento resinoso usando sistema adesivo autocondicionante de 1 passo de aplicação (PanaviaTM F, Kuraray, Osaka, Japan); e grupo IV: cimento resinoso auto-adesivo (BisCemTM, Bisco Inc., Schaumburg, IL). Cada grupo foi subdividido em dois subgrupos (N=10) variando-se o tempo de armazenagem (24 horas e seis meses). O teste de push-out foi realizado com uma velocidade de 1,0 mm/min, e os resultados expressos em Mega Pascal (MPa). Após o teste de push-out, todos os espécimes foram observados em microscópio óptico de fluorescência (40x) e analisado o tipo de falha apresentado entre o complexo pino/cimento/dentina radicular. Os valores médios de resistência (MPa) foram submetidos ao teste ANOVA a dois critérios e de Tukey (p<0,005). A análise estatística mostrou: 1) Diferenças significativas na resistência de união entre os cimentos utilizados, sendo que a média total do cimento resinoso RelyXTM ARC + ScotchbondTM MultipurposeTM foi superior aos dos outros cimentos após 24 horas; 2) A resistência de união dos cimentos resinosos RelyXTM ARC + ScotchbondTM MultipurposeTM e PanaviaTM F foram superiores aos outros cimentos quando testados após seis meses de armazenagem e não houve diferença significativa entre eles; 3) Após seis meses de armazenagem, observou-se um aumento na resistência de união de todos os cimentos; 4) Na análise por terços, foi observado que tanto após 24 horas quanto após seis meses, o terço cervical teve uma maior resistência de união do que o terço médio e apical; 5) Foram observadas predominantemente falhas mistas, apresentado-se na maioria dos casos a combinação de falha adesiva na interface pino/cimento e na interface cimento/dentina para todos os grupos. Concluiu-se que a resistência de união aumentou após seis meses de armazenagem graças possivelmente à expansão higroscópica e aumento da retenção friccional. / The bond strength of a glass fiber post luted to dentin with four luting agents was evaluated using the push-out test, after 24-hours and six months of storage. Eighty human single-routed teeth was selected, endodontically treated and randomly divided into four groups (n=20), modifying the luting agent used: group I: resin modified glass-ionomer (Fuji PlusTM, GC Corp., Tokyo, Japan); group II: resin cement using total-etch, three step adhesive system (RelyX ARC + Scotchbond Multi-purpose, 3M ESPE, St Paul, MN, USA); group III: resin cement using self-etch one step adhesive system (PanaviaTM F, Kuraray, Osaka, Japan); and group IV: self-adhesive resin cement (BisCemTM, Bisco Inc., Schaumburg, IL). Each group was, then, subdivided into two subgroups (n=10) modifying the storage period (24-hours and six months). The push-out test was performed with a cross-speed of 1,0 mm/min, and the results expressed in Mega Pascal (MPa). After the test, all specimen interfaces were examined with the aid of a fluorescence optic microscope (40x) to dertemine the type of failure at the complex post/cement/dentin. The mean values of the bond strength (MPa) were analyzed with the two-way ANOVA and Tukey test (p<0,005). The statistical analysis showed: 1) Significant difference in the bond strength between the luting agents, in wich the mean total value of the resin cement RelyXTM ARC + ScotchbondTM MultipurposeTM was the highest after 24 hours; 2) The bond strength of the resin cement RelyXTM ARC + ScotchbondTM MultipurposeTM and PanaviaTM F were higher than the others luting agents when evaluated after six months, and there was no significant difference among both of them; 3) An increase in the bond strength of all luting agents after six months of storage in distilled water; 4) That the cervical third had a higher bond strength compared to the middle and apical thirds for all materials, during third analysis after 24-hours and six months of storage; 5) Predominantly, it was observed mixed failures, in the majority of the cases, with a combination of adhesive failure in the post/luting agent interface and in the luting agent/radicular dentin interface. Therefore, can be concluded that the bond strength of a glass fiber post luted to dentin with different luting agents can increase after six months of storage, possibly contributed by hygroscopic expansion and the increase of the frictional retention.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-16042009-112430
Date02 December 2008
CreatorsTawil, Rosalyn Chidiak
ContributorsValle, Accacio Lins do
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0019 seconds