The extent of BiInO3 substitution in the perovskite system xBiInO3-(1-x)PbTiO3 and the corresponding raise in the Curie temperature were investigated using thermal analysis, X-ray diffraction and electron microscopy. Maximum tetragonal perovskite distortion (c/a = 1.082) was obtained for x=0.20, with a corresponding Curie temperature of 582C. Phase-pure tetragonal perovskite was obtained for x less than 0.25. Compound formation after calcining mixed oxide powders resulted in agglomerated cube-shaped tetragonal perovskite particles, which could be fired to 94.7% of theoretical density (TD) by crushing after calcining, dry pressing and firing. Sol-gel fabrication resulted in nano-sized tetragonal or pseudo-cubic perovskite particles, which after two-step firing, resulted in a tetragonal perovskite microstructure at as high as (x=0.25) 98.2% of TD.
Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/5114 |
Date | 10 June 2004 |
Creators | Duan, Runrun |
Publisher | Georgia Institute of Technology |
Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
Language | en_US |
Detected Language | English |
Type | Thesis |
Format | 2712123 bytes, application/pdf |
Page generated in 0.0016 seconds