O titanato e zirconato de chumbo \'PB\'(\'ZR\'1-y\'TI\'y)\'O IND.3\' é um material ferroelétrico de estrutura perovskita que tem sido aplicado como transdutores, amplificadores, sensores piezoelétricos, piroelétricos e memórias ferroelétricas. É bem estabelecido que a incorporação de íons de \'LA POT.3+\' ou \'BA POT.2+\' nos sítios ocupados pelo \'PB\' no sistema \'PB\'(\'ZR\'1-y\'TI\'y)\'O\' (PZT), formando os sistemas \'PB\'1-x\'LA\'x\'ZR\'1-y\'TI\'y\'O IND.3\' (PLZT) e \'PB\'1-x\'BA\'x\'ZR\'1-y\'TI\'y\'O IND.3\' (PBZT), provoca mudanças significativas nas suas propriedades. No entanto, poucos trabalhos tem sido dedicados a esses sistemas contendo altas concentrações de \'TI\', principalmente no que se refere à estrutura desses materiais. Assim, este trabalho teve por objetivo analisar as propriedades estruturais e suas correlações com as propriedades dielétricas dos sistemas \'PB\'1-x\'LA\'x\'ZR\'0,40\'TI\'0,60\'O IND.3\' (PLZT100x) e \'PB\'1-x\'BA\'x\'ZR\'0,40\'TI\'0,60\'O IND.3\' (PBZT100x) em função da composição e da temperatura. Foram preparadas amostras cerâmicas por meio de sinterização convencional com x variando entre 0,05 e 0,21 para o sistema PLZT e entre 0,10 e 0,50 para o sistema PBZT. Em relação à estrutura a longa distância, medidas de difração de raios X mostraram uma diminuição no grau de tetragonalidade com o aumento da concentração dos cátions substituintes, que foi atribuída à formação de vacâncias no sítio A (caso do \'LA\') e diferença entre o raio iônico (caso do \'BA\'). Estas alterações estruturais em função da composição foram também responsáveis pelo aumento do grau de difusidade das curvas de permissividade dielétrica e pela observação de um estado ferroelétrico relaxor nas amostras contendo altas concentrações de \'LA\' e \'BA\'. Em relação à estrutural local, os resultados obtidos através da técnica de espectroscopia de absorção de raios X (XAS) nas bordas \'K\' do \'TI\' e LIII do \'PB\' mostraram que a incorporação de átomos de \'LA\' ou \'BA\' à estrutura do PZT leva a uma redução no deslocamento do átomo de \'TI\' em relação ao centro do octaedro \'TI\'O IND.6\' e mudanças na ordem local do átomo de \'PB\'. No que tange as composições contendo 21% at. de \'LA\' e 50% at. de \'BA\', diferentemente dos resultados de DRX que mostraram uma simetria cúbica, a técnica de XAS mostrou uma simetria local tetragonal. Em bom acordo com os resultados obtidos pela técnica de espectroscopia Raman, espectros EXAFS medidos em altas temperaturas mostraram também que a estrutura local não é compatível com uma estrutura de simetria cúbica. Espectros XANES medidos na borda \'K\' do oxigênio revelaram uma redução no grau de hibridização entre os estados 2p do \'O\' com 6sp do \'PB\' à medida que a concentração de \'LA\' ou \'BA\' aumenta, que estaria relacionada com o surgimento de comportamento relaxor. Amostras cerâmicas densas nanoestruturadas de composição PZT, PLZT11 e PBZT10 foram preparadas pelo método de spark plasma sintering (SPS) a fim de analisar a influência do tamanho de grão. Foi verificado que as amostras sinterizadas por SPS apresentam tamanho de grão em torno de 60 nm. A caracterização dielétrica destas amostras mostra que a redução do tamanho de grão causa uma redução no valor de máximo da permissividade dielétrica e características difusas da permissividade em função da temperatura devido ao aumento das regiões de contorno de grão. / Lead titanate zirconate (\'PB\'(\'ZR\'1-x\'TI\'x)\'O IND.3\') are ferroelectric materials with perovskite structure which has been used as transducers, capacitors, piezoelectric and pyroelectric sensors and ferroelectric memories. The substitution of \'PB POT.+2\' ions by \'LA POT.+3\' or \'BA POT.+2\' ions in the \'PB\'(\'ZR\'1-x\'TI\'x)\'O IND.3\' (PZT) system, which leads to the formation of the \'PB\'1-x\'LA\'x\'ZR\'1-y\'TI\'y\'O IND.3\' (PLZT) and the \'PB\'1-x\'BA\'x\'ZR\'1-y\'TI\'y\'O IND.3\' (PBZT) systems, induces several changes in the electric and structural properties of these materials. However, PLZT or PBZT systems based on \'TI\'-rich compositions have not been thoroughly investigated and the literature contains few reports concerning their structure. Thus, the main objectives of this doctoral thesis were the synthesis and structural characterization of \'PB\'1-x\'R\'x\'ZR\'0.40\'TI\'0.60\'O IND.3\' ferroelectric ceramic samples, with R = \'BA\' and \'LA\' and x between 0.00 to 0.50 (PLZT100x and PBZT100x). The characterization with X-ray diffraction technique of these samples showed a decrease of the tetragonality degree with increase of the doping cation concentration, which was related to the appearance of defects caused by the incorporation of \'LA\' or \'BA\' cations. These structural modifications were also responsible by the increase of the diffuseness at the dielectric permittivity and a relaxor behavior as a function of the \'LA\' or \'BA\' concentration. Concerning the local structure, XANES spectra in the absorption edge of various elements in PLZT and PBZT samples were performed. In the cases of \'TI\' \'K\'-edge absorption, the doping of \'LA\' and \'BA\' atoms in the PZT structure leads to a reduction of the displacement of \'TI\' atom in the center of the \'TI\'O IND.6\' octahedron. However, even when the crystal structure is cubic, a local octahedron distortion remains. EXAFS measurements in \'PB\' LIII-edge and \'ZR\' \'K\'-edge were performed and also indicate that local structure around lead or zirconium atoms is also affected by the introduction of \'LA\' and \'BA\' atoms in the PZT structure. In addition, XANES spectra measured at \'O\' \'K\'-edge revealed a reduction in the hybridization degree between \'O\' 2p and \'PB\' 6sp states with the addition of \'LA\' or \'BA\' atoms to the structure of PZT. It has been shown that hybridization between these states is essential to ferroelectricity and this reduction would be related to the relaxor behavior. PLZT and PBZT systems were also studied depending on the size of particle size in a nanometer scale. Thus samples PZT, PLZT11 and PBZT10 compositions were prepared using the synthesis method of precursor polymers and the process of sintering by spark plasma. A pronounced decrease in the values of maximum permittivity was observed and the dielectric curve as a function of the temperature exhibits a diffuse behavior. This size-induced diffuse phase transition and the reduction of the permittivity magnitude could be related to the differences between the core grain and the grain boundaries.
| Identifer | oai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-19042011-172117 |
| Date | 15 March 2011 |
| Creators | Mesquita, Alexandre |
| Contributors | Mastelaro, Valmor Roberto |
| Publisher | Biblioteca Digitais de Teses e Dissertações da USP |
| Source Sets | Universidade de São Paulo |
| Language | Portuguese |
| Detected Language | English |
| Type | Tese de Doutorado |
| Format | application/pdf |
| Rights | Liberar o conteúdo para acesso público. |
Page generated in 0.0028 seconds