The diploma thesis deals with phase composition measurement of the TRIP steel, using EBSD method. The steel was delivered as thermo-mechanically treated via two different routes. The phase composition of the steel was examined during gradual plastic deformation in the range 0 to10.99%. One route of thermo-mechanical treatment exhibited good agreement with the literature in terms of measured fraction of the retained austenite (15.6%) as well as its decrease during the deformation (to 8.9% at the maximum imposed strain). The samples of the second route did not show any agreement in either of the parameters spoken.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:228272 |
Date | January 2008 |
Creators | Pešina, Zbyněk |
Contributors | Pantělejev, Libor, Man, Ondřej |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds