Objectives. Polyamide-12 (PA) is a flexible material suited for denture bases and clasping. This study investigated its potential aging effects with a focus on surface roughness, color stability, and elasticity. Methods. PA specimens (Valplast) of 40 × 10 × 2mm and equally measuring PMMA specimens (Palapress) as control were fabricated. Color changes after storage in air, water, coffee, and red wine (n = 10) were measured using the CIE L*a*b color specification. Elasticity after thermocycling (1000, 3000, and 7000 cycles, n = 15) was measured by three-point bending testing. Mean surface roughness (Ra) was determined after storage in the liquids mentioned above and thermocycling (n = 10). Results. Tukey’s HSD test (P < 0.05) revealed statistically significant color changes of PA in red wine (ΔE = 4.27 after 12 days, EΔE = 6.90 after 12 days) and coffee (ΔE = 3.93 after 36 days) but no color changes in PMMA. Elastic modulus of PA was 845MPa and not affected by thermocycling (Tukey’s HSD test, P > 0.81). Dry specimens showed significantly decreased elasticity (P < 0.001). Mean surface roughness (PA 0.20 μm, PMMA 0.28 μm) did not change significantly after thermocycling or storage (Mann-Whitney U-test, 0.16 < P < 0.65). Significance. PA exhibited a higher susceptibility to discoloration than PMMA. Neither surface roughness nor elasticity of PA was altered by artificial aging.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:14-qucosa-147158 |
| Date | 07 July 2014 |
| Creators | Wieckiewicz, Mieszko, Opitz, Volker, Richter, Gert, Böning, Klaus W. |
| Contributors | Hindawi, |
| Publisher | Saechsische Landesbibliothek- Staats- und Universitaetsbibliothek Dresden |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:article |
| Format | application/pdf |
| Source | BioMed Research International, Volume 2014 (2014), Article ID 150289, ISSN: 2314-6133 |
Page generated in 0.0022 seconds