<p>Dynamic properties of type-II superconductors have been experimentally studied in zero and low magnetic fields using SQUID magnetometry and <i>I–V</i> measurements.</p><p>In zero magnetic field close to the critical temperature, the physical properties of type-II superconductors are dominated by spontaneously created vortices. In three dimensions (3D) such vortices take the form of vortex loops and in two dimensions (2D) as vortex-antivortex pairs.</p><p>The 2D vortex dynamics has been probed using mutual inductance and flux noise measurements on YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7</sub> (YBCO) and MgB<sub>2</sub> thin films in zero and low magnetic fields. In such measurements, information about vortex correlations is obtained through a temperature dependent characteristic frequency, below (above) which the vortex movements are uncorrelated (correlated). The results obtained in zero magnetic field indicate that sample heterogeneities influence the vortex physics and hinder the divergence of the vortex-antivortex correlation length.</p><p>In low magnetic fields the vortex dynamics is strongly dependent on the applied magnetic field and a power law dependence of the characteristic frequency with respect to the magnetic field is observed. The results indicate that there is a co-existence of thermally and field generated vortices.</p><p>The <i>I–V</i> characteristics of untwinned YBCO single crystals show that only a small broadening of the transition region influences the length scale over which the vortex movements are correlated. The dynamic and static critical exponents therefore exhibit values being larger in magnitude as compared to values predicted by relevant theoretical models. The results also suggest that the copper oxide planes in YBCO decouple slightly below the mean field critical temperature and hence, the system has a crossover from 3D to 2D behaviour as the temperature is increased. </p><p>From temperature dependent DC-magnetisation measurements performed on untwinned YBCO single crystals in weak applied fields, detailed information about the critical current density and the irreversibility line is obtained.</p>
| Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:uu-3907 |
| Date | January 2003 |
| Creators | Festin, Örjan |
| Publisher | Uppsala University, Department of Engineering Sciences, Uppsala : Acta Universitatis Upsaliensis |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, text |
| Relation | Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1104-232X ; 919 |
Page generated in 0.0014 seconds