Influ?ncia de tratamentos t?rmicos de recozimento na microestrutura de uma liga NiTi pseudopl?stica

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-12-01T23:25:13Z
No. of bitstreams: 1
ThiagoSouzaViana_DISSERT.pdf: 4828616 bytes, checksum: ee06ed8ff3676ebb8c30b440a888b38d (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-12-05T20:32:59Z (GMT) No. of bitstreams: 1
ThiagoSouzaViana_DISSERT.pdf: 4828616 bytes, checksum: ee06ed8ff3676ebb8c30b440a888b38d (MD5) / Made available in DSpace on 2017-12-05T20:32:59Z (GMT). No. of bitstreams: 1
ThiagoSouzaViana_DISSERT.pdf: 4828616 bytes, checksum: ee06ed8ff3676ebb8c30b440a888b38d (MD5)
Previous issue date: 2017-06-30 / No presente trabalho, estudou-se a influ?ncia de tratamentos t?rmicos nas transforma??es microestruturais de uma liga NiTi com mem?ria de forma de composi??o qu?mica aproximadamente equiat?mica. Um fio de NiTi com 2,5 mm de di?metro, recebido no estado encruado, foi submetido a tratamentos t?rmicos de recozimento em temperaturas de 450 ?C e 500 ?C para observa??o das varia??es microestruturais. As microestruturas predominantes antes e ap?s o recozimento foram observadas, registrando-se um aumento na granulometria da martensita tanto com a temperatura como com a dura??o do tratamento t?rmico entre 30? e 3hs. Foram determinadas as temperaturas de transforma??o, (As, Af, Ms, Mf) de cada amostra, e as altera??es nas temperaturas de transforma??o entre o material no estado encruado e ap?s recozimento. Medidas de microdureza n?o revelaram influ?ncia significativa de tratamentos t?rmicos de recozimento e tampouco de resfriamentos a temperaturas subzero. / In the present work, the influence of heat treatments on the microstructural transformations of an approximately equiatomic NiTi memory form alloy was investigated. A NiTi wire with 2.5 mm in diameter, received in the work hardened state, was submitted to annealing heat treatments at 450 ?C and 500 ?C in order to verify the calorimetric and microstructural changes. The microstructure in the work hardened condition and after the annealing heat treatments was analyzed, which showed a coarsening of the martensite plates for higher temperatures and longer heat treatment times. The determination of the transition temperatures (As, Af, Ms, Mf) and the change in the transformation temperatures between the as received worked hardened and annealed material, were determined. Microhardness measurements did not reveal any significant influence of the annealing or subzero heat treatments on the mechanical behavior of the alloy.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/24414
Date30 June 2017
CreatorsViana, Thiago Souza
Contributors30399564853, Castro, Nicolau Apoena, 27783773877, Nascimento, Rubens Maribondo do, 80732810400, Castro, Walmam Ben?cio de, 39614638400, Buschinelli, Augusto Jos? de Almeida
PublisherPROGRAMA DE P?S-GRADUA??O EM CI?NCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds