This study aimed at dissimilar metal butt friction stir welding in various types of processing conditions on the welding product hardness, tensile strength, etc.
At first, using the AA-5052 as the similar material in FSW(friction stir welding) process. Compare the affected in different working parameter such like tool rotation speed, tool feed rate, etc. During FSW process, using the K-type thermal couple to monitoring the temperature history at different position in the specimen. According the result and finding the best working parameter.
As the result shown, the high speed rotating rate or the low feeding rate will cause more heat energy in the specimen. In completed FSW condition, the range of rotating rate is 600-900rpm, the feeding rate is 40-80mm/min, the preheating temperature is suitable in 350¢J.
For the aluminum alloy and copper alloy of the dissimilar metal friction stir welding, specimen¡¦s surface has holes and large chip by lacking heat during using the tool diameter of 12mm to weld, use the tool diameter of 15mm to weld can enhance the heat during the welding process and improve the production of surface.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0831109-152828 |
| Date | 31 August 2009 |
| Creators | Lin, Chien-Hua |
| Contributors | Woei-Shyan Lee, Yeong-Maw Hwang, Fuh-Kuo Chen |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0831109-152828 |
| Rights | campus_withheld, Copyright information available at source archive |
Page generated in 0.0158 seconds