Influência das tensçoes residuais no comportamento em fadiga e fratura de ligas metálicas

Submitted by Marcele Costal de Castro (costalcastro@gmail.com) on 2017-12-14T13:05:21Z
No. of bitstreams: 1
MARIA DA CONCEIÇÃO BARBOSA VIEIRA SOARES D.pdf: 7820788 bytes, checksum: 8508cf257a678320eed219e7cd7d8efa (MD5) / Made available in DSpace on 2017-12-14T13:05:21Z (GMT). No. of bitstreams: 1
MARIA DA CONCEIÇÃO BARBOSA VIEIRA SOARES D.pdf: 7820788 bytes, checksum: 8508cf257a678320eed219e7cd7d8efa (MD5)
Previous issue date: 1998 / Tensões residuais compressivas podem ser introduzidas na superfície de componentes mecânicos através de processos de fabricação como tratamentos térmicos, autofretagem e jateamento por partículas. Em geral estas tensões residuais são benéficas e aumentam a resistência do material à fratura, à iniciação e ao crescimento de trinca. Neste trabalho as tensões residuais induzidas pelo processo de jateamento por partículas em quatro ligas metálicas, de diferentes estruturas cristalinas e sob diversas condições de jateamento foram obtidas por difração de nêutrons. O fator de intensificação de tensões K destas tensões residuais foi determinado pelo método dos elementos finitos e da função ponderação utilizando como modelo para o método de elementos finitos uma placa contendo uma trinca lateral. O efeito da aplicação simultânea da tensão residual e de tensão remota no fator de intensificação de tensões K foi avaliado. O processo de jateamento por partículas melhorou a resistência ao trincamento na maioria dos materiais estudados. O efeito de sobreposição de trinca também foi considerado, para determinação correta dos valores de intensificação de tensões K. O trabalho investiga também a influência do processo de jateamento por partículas na vida em fadiga de baixo ciclo, sob condições de controle de deslocamento e dobramento em quatro pontos, de uma superliga de níquel (Waspaloy). Avaliação microestrutural por microscopia ótica e eletrônica foi efetuada para auxiliar na determinação das causas do modo de fratura intergranular à temperatura ambiente. / Compressive residual stresses are beneficial and improve resistance to fracture and crack growth. Residual stresses can be introduced in fabricated components by a variety of means and a number of methods such as surface treatments, cold expanded hole and shot peening. Neutrons diffraction measurements of residual stresses induced by shot peening on four metallic materials under different intensity conditions were performed at nuclear reactor. The stress intensit>' factor K of residual stress was evaluated by finite element modelling and weight function method. Finite element modelling of a plate with a single edge-notch was applied: The stress intensity factor K was evaluated for both case of remote stress and residual stress. Shot peenning significantly improved the resistance of cracking on almost all materials in the present investigation. Crack surface overlapping, which is physically unacceptable, was noted for small cracks under residual and boundary loading. Overlap correction was proposed and applied in order to obtain reliable values for K. Low cycle fatigue experiments of peened and unpeened specimens of Waspaloy were performed under displacement control and four point bend. A microstructural evaluation by optical and electron microscopy was done in order to find the causes of intergranular fracture at room temperature.

Identiferoai:union.ndltd.org:IBICT/oai:carpedien.ien.gov.br:ien/2028
Date January 1998
CreatorsSoares, Maria da Conceição Barbosa Vieira, Instituto de Engenharia Nuclear
ContributorsAndrade, Arnaldo H. Paes de
PublisherInstituto de Engenharia Nuclear, Programa de Pós-Graduação em Engenharia de Reatores Nucleares de Potência e Tecnologia do Combustível Nuclear, IEN, Brasil, Instituto de Pesquisas Energéticas e Nucleares
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Repositório Institucional do IEN, instname:Instituto de Engenharia Nuclear, instacron:IEN
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds