O presente trabalho teve por objetivo quantificar, comparativamente, a área de preenchimento de dois materiais obturadores sólidos, cones de guta-percha (GP) e cones de Resilon (R), no terço apical de incisivos inferiores humanos, ex vivo, obturados pela técnica da onda contínua de condensação. Os espécimes foram submetidos a um protocolo, desde a cirurgia de acesso até o final do preparo químico-mecânico e divididos aleatoriamente em dois grupos, de 21 dentes cada, de acordo com o material utilizado. Não foi utilizado cimento endodôntico em nenhuma das amostras. Após a obturação, as amostras foram seccionadas transversalmente em dois níveis, a 3 e a 5mm do ápice, e subdivididas em grupos de acordo com a altura de corte e do material obturador, sendo estabelecido: GP3 (guta-percha com corte a 3mm), GP5 (guta-percha com corte a 5mm), R3 (Resilon com corte a 3mm) e R5 (Resilon com corte a 5mm). Posteriormente, as amostras foram submetidas a um processo de lixamento e polimento e examinadas em microscópio óptico por reflexão com aumento de 50x a 100x. Para a análise e processamento digital das imagens, foi utilizado o sistema de imagens Axio Vision 4.6 para Windows, sendo obtidas as medidas para cada área observada em micrômetros (μm); uma da área da cavidade, e outra da área de material obturador. Foi aferido o grau de circularidade de cada amostra, por uma fórmula matemática utilizada automaticamente pelo programa, onde 1 (um) é considerado o círculo perfeito e, quanto mais achatado o canal, mais tendente a 0 (zero) nesta escala. Obteve-se a área do canal, a circularidade de 0 a 1, a área preenchida pelo material obturador e, a porcentagem da área de preenchimento do material obturador em relação à área do canal. Foi realizado o cruzamento dos grupos dois a dois pelo teste t de Student, sendo verificada diferença estatisticamente significante entre os grupos GP3 e R3, tendo o grupo R3 apresentado maior porcentagem de área do canal radicular preenchida pelo material obturador em suas amostras (p<0,05). Na relação da circularidade com a quantidade de preenchimento, com o teste de Correlação de Pearson, não foi observada forte correlação entre a forma final do canal (relação de circularidade) e a quantidade de preenchimento do canal radicular pelos materiais obturadores testados. Conclui-se que houve grande variação de preenchimento mínimo e máximo em todos os grupos testados e o Resilon apresentou maior porcentagem de preenchimento de área do canal radicular em suas amostras. / The aim of this study was to determine a quantitative comparison of gutta-percha and Resilon filled areas in the apical third of human mandibular incisors, ex vivo, after obturation by continuous wave condensation technique. The tooth samples were submitted to irrigation and instrumentation protocol and randomly divided in two groups of twenty-one each. No sealer was used. After obturation, a horizontal section was cut 3mm and 5mm from the apical foramen of each tooth. The two groups were subdivided according to cut height and obturation material as follows: GP3 (gutta-percha with 3mm section), GP5 (gutta-percha with 5mm section), R3 (Resilon with 3mm section) e R5 (Resilon with 5mm section). The samples were later prepared for microscopic analysis and photomicrographs of each apical surface were taken at magnifications from 50x to 100x. The cross-sections of the canal areas with the obturation materials were measured using an image analysis program, obtaining the measurement of each canal area and filled area in micrometers. The circular form of each sample was rated automatically by a mathematic formula used by the program, where 1 (one) is considered a perfect circle, and as it flattens, the value approaches 0 (zero). The digital imaging analysis obtained the canal area, the circular form from 0 to 1, the area filled by obturation material, and the percentage of material filled area relative to the canal area. The percentage difference of the filled canal area among the groups was analyzed using a Students t-test. Significant differences were found between GP3 and R3. The greatest percentage of filled canal area occurred in the R3 group (p<0,05). With respect to the relationship of the circular form with the quantity of filling material, by using the Pearson Correlation test, no significant correlation was found between the final form of the canal and the quantity of root canal filling by the obturation materials tested. In conclusion, a great variation in the minimum and maximum filled percentage occurred all groups tested and the Resilon group showed a higher percentage of filled root canal area in their samples.
Identifer | oai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:UERJ:oai:www.bdtd.uerj.br:1889 |
Date | 22 February 2008 |
Creators | Marcello Ghetti de Melo |
Contributors | Teresa Cristina Ávila Berlinck, Luciana Moura Sassone, Rivail Antonio Sergio Fidel, Antonio José Ribeiro de Castro, Yara Teresinha Correa Silva Sousa |
Publisher | Universidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Odontologia, UERJ, BR |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds