In preparation for the large backgrounds expected to be present in the Belle II detector from the SuperKEKB e+e- collider, the radiation hardness of several large (5 x 5 x 30 cm3) thallium doped cesium iodide (CsI(Tl)) scintillation crystals are studied. The crystal samples studied consist of 2 spare crystals from the Belle experiment using PIN diode readout and 7 spare crystals from the BaBar experiment using photomultiplier tube readout. The radiation hardness of the scintillation properties of the CsI(Tl) crystals was studied at accumulated 1 MeV photon doses of 2, 10 and 35 Gy. At each dose, the longitudinal uniformity of the crystals light yield, scintillation decay times, time resolution and energy resolution was measured. As the Belle II collaboration is considering an upgrade to pure CsI crystals if CsI(Tl) does not satisfy radiation hardness requirements, the scintillation properties of a pure CsI scintillation crystal were also measured and compared to the CsI(Tl) crystal measurements. In addition to experimental work, Monte Carlo simulations using GEANT4 were written to compare ideal pure CsI and CsI(Tl) crystals and to study the effects of radiation damage on the performance of the Belle II electromagnetic calorimeter. / Graduate
| Identifer | oai:union.ndltd.org:uvic.ca/oai:dspace.library.uvic.ca:1828/6707 |
| Date | 22 September 2015 |
| Creators | Longo, Savino |
| Contributors | Roney, J. Michael |
| Source Sets | University of Victoria |
| Language | English, English |
| Detected Language | English |
| Type | Thesis |
| Rights | Available to the World Wide Web |
Page generated in 0.0019 seconds