A study of the role of different oxidants with silicon as the fuel in simple binary pyrotechnic compositions is reported. Several oxidants were examined, but only three (Sb₂0₃, Fe₂0₃ and Sn0₂) satisfied the restrictions that the combustion temperatures should be below the melting point of platinum/rhodium thermocouples (1760°C), that burning rates should not exceed the response of the thermocouples, and that burning should occur without significant mass-transport. A fourth oxidant, KN0₃, was selected on account of its low melting point and general importance as a pyrotechnic oxidant. The oxidation of silicon in the presence of either Sb₂0₃ or KN0₃ could be identified from thermal analysis curves. No thermal events were noted when Si/Sn0₂ and SiFe₂0₃ compositions were heated under similar conditions. The oxidation of Si powder in oxygen was also studied. All four binary systems sustained burning over a reasonably wide range of compositions. The range of burning rates measured (2 to 35 mm s⁻¹) depended on the oxidant used. Fe₂0₃ and Sb₂0₃ gave slow burning mixtures compared to Sn0₂ and to KN0₃ compositions with a high Si content. Burning rates generally increased with increasing specific surface area of silicon, but decreased in the presence of inert diluents and moisture. The burning rates of the Si/Fe₂0₃ and Si/Sn0₂ systems increased with increasing compaction of the samples. Kinetic parameters derived from the temperature proftles recorded during combustion were generally low (6 to 37 kJ mol⁻¹). This is in keeping with proposals that burning is diffusion controlled. The values of kinetic parameters derived from thermal analysis curves were considerably greater ( > 250 kJ mol⁻¹). Two other fuels, FeSi₇ and CaSi₂, gave similar thermal analysis curves when used instead of silicon. There were considerable differences in the burning rates for binary mixtures of these fuels compared to silicon. Ternary systems with two fuels or two oxidants showed that only limited interaction occurs during thermal analysis. The use of a second fuel or oxidant did, however, modify the burning behaviour considerably. Other techniques used in this study to probe the details of the reaction processes included bomb calorimetry, measurement of thermal conductivities, infrared spectroscopy, X-ray diffraction and scanning electron micoscropy.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:rhodes/vital:4527 |
| Date | January 1992 |
| Creators | Rugunanan, Rajan Anil |
| Publisher | Rhodes University, Faculty of Science, Chemistry |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Doctoral, PhD |
| Format | 256 leaves, pdf |
| Rights | Rugunanan, Rajan Anil |
Page generated in 0.0018 seconds