The main subject of this master’s thesis was to evalute inluence of loading cycle asymmetry and long-term thermal exposure on fatigue crack growth rate in martensitic P91 and P92 steels. Experiments were carried out in Material and metallurgical research Ostrava Ltd. and their main aim was to study the influences of different loading cycle asymmetries (R = 0,1 and R = 0,6) as well as 5000 hours/600 °C (P91) respectively 5000 hours/650 °C (P92) of thermal exposure on fatigue crack growth rate.