This thesis deals with the issue of thermal spraying by means of an electric arc. First of all, a theoretical part is processed using a literary study dealing with corrosion and thermal spraying technology. The experimental part contains a description of the technological procedure and evaluation of four thermally sprayed samples. Zinacor 850, consisting of 85% zinc and 15% aluminum, was used as a coating. The evaluation involves measurements of thickness, adhesion and roughness as well as the macro-structural analysis of the coating. Two samples showed unusually low adhesion, and all samples also had a large fluctuation of the measured thicknesses. This was also confirmed by the macro-structural analysis, which showed that the sample with low adhesion also had high porosity. These defects may have multiple causes, but the recommendation for further practice is to reduce the spraying distance from the base material.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:417133 |
| Date | January 2020 |
| Creators | Eliáš, Vojtěch |
| Contributors | Sigmund, Marian, Kubíček, Jaroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds