Atomic Layer Epitaxy is a stepwise deposition process by supplying the sources materials alternatively. This deposition technique provides the monolayer control of film thickness and the uniform film growth over a large area. ZnSxSe1-x layers were grown epitaxially onto Si and GaAs substrate by using DMZn and H2S , H2Se gases for the reactant source. Owing to the self-limiting characteristics of ALE process, ZnSxSe1-x monolayers could be deposited over a wide range of temperature within growth window. In this study, for obtaining high crystalline quality ZnSxSe1-x epitaxial films, various growth conditions were investigated including substrate temperature, the flow rate of DMZn, H2S and H2Se, H2 purge duration and pulse duration etc..
A thermodynamic analysis based the calculation of Seki et. al [6], was used to investigate the effects by varying the substrate temperature, input mole ratio of group VI source gases on equilibrium partial pressure, solid composition and solid-vapor distribution relation of this alloy. The interaction parameter of ZnSxSe1-x, £[, was estimated by using the delta-lattice parameter (DLP) model suggested by Stringfellow [39]. Finally, it shows that the thermodynamic analysis provides a useful guideline for the growth of ZnSxSe1-x alloy on Si and GaAs substrates.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0703103-102111 |
| Date | 03 July 2003 |
| Creators | Wang, Hong-Yi |
| Contributors | Ai-Na Hung, Wei-Chou Hsu, Cheu-Pyeng Cheng, Uerng-Yih Ueng, Yen-Sheng Lin |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0703103-102111 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.001 seconds