This thesis deals with fabrication and optimization of lead-free piezoceramics based on (Ba0,85Ca0,15Zr0,1Ti0,9)O3 (BCZT). The BCZT precursor powder was synthesized by sol-gel method. Dependence of relative density, microstructure, phase structure and piezoelectric properties on the sintering temperature in a range from 1300–1500 °C was studied on disc shaped samples, which were prepared by cold isostatic pressing (CIP) using pressure of 700 MPa. It was found, that sintering at 1300 and 1350 °C leads to ceramics with fine-grain microstructure, which exhibits poor piezoelectric properties (d*33 = 50 pC·N1 and 65 pC·N1, respectively). The highest value of piezoelectric charge coefficient was obtained by sintering at 1500 °C (d*33 = 390 pC·N1). Furthermore, BCZT thick films were prepared by tape casting. The composition of the ceramic slurry was optimized and various sintering techniques were tested to obtain completely flat films of BCZT ceramics. The correct sintering configuration has not been found. The least deformation of the films was achieved when the samples were sintered hung on the ZrO2 rod. The highest value of d*33 for BCZT films was measured when the sample was sintered at 1400 °C with the dwell time for 4 h (d*33 = 340 pC·N1).
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:401844 |
| Date | January 2019 |
| Creators | Fojtík, Ondřej |
| Contributors | Holcman,, Vladimír, Tofel, Pavel |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds