Previous issue date: 2003-08 / A Paraíba se destaca no mercado nacional de calçados ocupando o quinto lugar em exportação. Algumas dessas indústrias utilizam um tipo de polímero o EVA (etilene vinil acetate), para fabricação de palmilhas e solados de calçados. O destino final dos resíduos gerados parece ser os lixões e aterros clandestinos. Esses resíduos consistem de restos de placas provenientes do processo de corte para fabricação do calçado e de um pó resultante da fase de acabamento. Uma maneira de livrar o meio ambiente dos inconvenientes causados pela geração desses resíduos é a sua incorporação em tijolos de terra crua, tema desta dissertação. Foram inicialmente feitos ensaios de caracterização dos materiais empregados. Foram testadas várias combinações do teor de solo-EVA, tendo o teor desses resíduos variado de 0 a 50% em relação ao volume de solo. Para o emprego do resíduo que se apresenta em forma de placas adotou-se a trituração em moinho rotativo para produzir partículas menores que 2,4 mm. No caso do resíduo em pó não houve nenhum processo de transformação. Como estabilizante foi usado o cimento em taxas de 6, 8 e 10% em relação ao peso do solo. Foram obtidas as resistências à compressão de tijolos prensados em uma pequena prensa manual, com diversas misturas. Com algumas destas misturas fabricaram-se tijolos com os quais
foram moldados quatro painéis com cerca de lm2 . Eles foram instrumentados com 5
extensômetros para acompanhamento das deformações e procedeu-se o ensaio de compressão simples. Também foram construídas duas paredes, uma com incorporação de EVA e outra sem, para comparação do desempenho térmico. Os resultados mostraram que à medida que se aumentou o teor de EVA a resistência dos tijolos caiu sensivelmente. Mais de 10% de incorporação é inconveniente. O comportamento das paredes foi satisfatório, porém com o equipamento utilizado não se consegue compactar o solo adequadamente e por conseguinte as resistências não foram elevadas, porém satisfatórias para muros divisórios não estruturais. Do ponto de vista térmico, mostrou-se que a incorporação de apenas 10% de borracha conduziu a uma diminuição de aproximadamente 5 °C em relação a parede de tijolos sem EVA,
expostos às mesmas condições de contorno. / Concerning shoes export, Paraíba state is in the fifth place in Brazil. Some of these industries
use a type of polymeric EVA (Etilene vinyl acetate) that generate many waste that causes
problems to environment. Two types of residues are present: in form of plates and as a
powder. A way to liberate the environment of that inconvenient material is its incorporation in
compressed earth blocks as shown in this work. The characterization of the materiais was
made. Several mixtures soil-EVA were tested, with the percentage of residues varying from 0
to 50% in relation to the soil volume. To employ of the residue, that comes in form of plates
a mill was used to produce particles smaller than 2,4 mm. In the case of the powdered residue,
none transformation process was needed. As stabilizer, cement was used in rates of 6, 8 and ^
10% by weight of soil. Compression strength of the mixtures was obtained in the bricks, ^
fabricated in a small manual press. With some of these mixtures bricks were manufactured £o
and four paneis with about lm2 were built. They were instrumented with 5 strain gages and a ™
compression test was made. Two others walls, one with incorporation of EVA and another £j
without, were prepared for thermal performance. Results show that increasing the amount of ^
EVA strength of the bricks drops sensibly. More than 10% of EVA incorporation are not
adequate. The walls performed well, even if the press with doesn't get great compactation on
the soil and consequently the resistances were not high. They can be used for non-structural
walls. In the thermal point of view, it is shown that the incorporation of 10% of rubber drove
to a decrease of approximately 5 °C in relation to a wall made with bricks without EVA,
exposed to the same boundary conditions.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/933 |
Date | 12 June 2018 |
Creators | SILVA, Elisângela Pereira. |
Contributors | BARBOSA, Normando Perazzo., NASCIMENTO, José Wallace Barbosa do., NEVES, Gelmires Araújo., BERALDO, Antônio Ludovico. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA AGRÍCOLA, UFCG, Brasil, Centro de Tecnologia e Recursos Naturais - CTRN |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Relation | SILVA, Elisângela Pereira da. Incorporação de resíduos da indústria de calçados (EVA- etilene vinil acetate) em tijolos prensados de terra crua. 2003. 99f. Programa de Pós-graduação em Engenharia Agrícola, Centro de Tecnologias e Recursos Naturais, Universidade Federal de Campina Grande – Paraíba – Brasil, 2003. |