Aspectos da furação do titânio 6Al4V com broca de aço rápido sinterizado e broca de metal duro / Drilling aspects from titanium 6Al4V with sintered high speed steel drill and carbide drill

Made available in DSpace on 2015-03-03T11:52:43Z (GMT). No. of bitstreams: 0
Previous issue date: 2014-07-14Bitstream added on 2015-03-03T12:07:08Z : No. of bitstreams: 1
000807370.pdf: 2293849 bytes, checksum: d68b7cab07938392e6c6fbc74359add9 (MD5) / As exigências e a competitividade atual levam, cada vez mais, à busca por soluções mais baratas e eficazes, para qualquer segmento de mercado. Com isso, o ramo aeronáutico tem procurado por ferramentas que possibilitem o mais alto rendimento possível aliado à redução de custos. Este trabalho de furação em placas de titânio 6Al4V tem origem em função da comunalidade de uso deste material nas indústrias, por manter alta resistência mecânica e a altas temperaturas. As ferramentas escolhidas foram brocas de metal duro e brocas de aço rápido sinterizado objetivando um estudo comparativo entre estas, nas mais variadas condições de corte, desde a refrigeração em abundância com utilização de óleo solúvel, passando pela usinagem à seco e finalizando com o sistema da Mínima Quantidade de Lubrificação (MQL) com óleo de corte puro. Os parâmetros de corte adotados foram conforme literatura técnica, para brocas de metal duro, utilizou-se velocidade de corte de 28 m/min, avanço total de 72 m/min e rotação de 2123 RPM e para as brocas de aço rápido sinterizado, velocidade de corte de 11 m/min, avanço total de 29 mm/min e rotação de 876 RPM. Anterior ao inicio dos testes, foi aplicado a ferramenta de Análise do Modo e Efeito de Falha a fim de identificar e prevenir possíveis discrepâncias na execução do processo de furação. A usinagem ocorreu em passes de 8mm de profundidade com interrupção a cada 200mm a 250mm para recolhimento de amostra de cavaco e avaliação parcial dos diversos possíveis desgastes nas ferramentas. Os parâmetros iniciais de finalização de cada broca foram estabelecidos com desgaste de 0,1mm ou tolerância de furos finais acima de H12. Os testes foram repetidos para ambas as brocas sempre em condições idênticas a fim de permitir uma comparação de resultados entre as ferramentas, geração ... (Resumo completo, clicar acesso eletrônico abaixo) / The current requirements and the competitiveness lead, increasingly, to the search for cheaper and more effective solutions, to any segment of the market.Thus the aeronautics the aviation industry has been searching for tools that allow the highest possible income combined with the cost reduction.. This work of drilling in 6Al4V titanium plates originates due to the commonality of use of this material in industries, for maintaining high mechanical strength and high temperatures. The tools chosen were carbide drills and drills of sintered high speed steel aiming at a comparative study between these, in the most varied cutting conditions, since refrigeration in abundance with use of oil soluble, through dry machining and finishing with the system of Minimal Quantity of Lubrication with neat cutting oil. The cutting parameters were adopted as technical literature, for carbide drills, used cutting speed of 28 m/min, total advance of 72 m/min and 2123 RPM rotation and sintered high speed steel drills, cutting speed of 11 m/min, total advance of 29 mm/min and 876 RPM rotation. Prior to the start of the tests, was applied to the analysis tool mode and effect of failure in order to identify and prevent possible discrepancies in the execution of the drilling process. The machining occurred in 8 mm deep steps with interruption every 200 mm to 250 mm for chip sample and partial evaluation of the various possible wear on tools. The initial parameters of completion of each drill were set with 0,1mm wear or tolerance of final holes above H12. The tests were repeated for both drills always in identical terms in order to allow a comparison of results between the tools, chip generation and final diameter. The diameters were measured with standard pins every 20 holes where, even after intense damage, there was no pre-established dimensional limits variation i.e. ... (Complete Abstract click electronic access below)

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/115929
Date14 July 2014
CreatorsAllegrini, Alex [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Ribeiro, Marcos Valério [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format123 f. : il.
SourceAleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation-1, -1

Page generated in 0.0024 seconds