The PhD thesis deals with the influence of temperature and strain rate on the mechanical behaviour of the Ti-6Al-4V titanium alloy. After verification tests under static loading conditions, the samples were deformed at high strain rates and elevated temperatures, using device for Hopkinson pressure bar test. The result is dependence of stress and strain rate on strain in the temperature range of 20 to 500°C. The deformed shape of specimen from the Taylor anvil test is compared with the results of the simulation in the Ansys – LS Dyna software. The parameters of Johnson-Cook equation were determined from these experiments. Also, the influence of loading conditions on the microstructure was studied. Both optical and scanning electron microscopes were used for the observations. During the research, some adjustments to the experimental devices were made in order to suppress the high-frequency components and noise in the recorded pulses. A functional tensile test adapter for the Hopkinson test was developed; it is registered under No. 2007/008 at the Technology Transfer Office of BUT.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:234028 |
| Date | January 2012 |
| Creators | Šlais, Miroslav |
| Contributors | Spišák, Emil, prof. Ing. Milan Turňa, Ph.D., EWE, IWE, Forejt, Milan |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0023 seconds