Efeito de um agente antioxidante e de solventes organicos adesivos sobre a resistencia de união ao esmalte humano tratado com peroxido de carbamida a 10% / Effect of an antioxiding agent on blond strebgth to human enamel treated with 10% carbamide peroxide

Orientador: Giselle Maria Marchi Baron / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T09:17:29Z (GMT). No. of bitstreams: 1
Silva_AnaPaulaBritoda_M.pdf: 2693552 bytes, checksum: b8df241111c3d0d8f3d4ba79d1bf4688 (MD5)
Previous issue date: 2005 / Resumo: O objetivo deste estudo in vitro foi avaliar o efeito de um gel de ascorbato de sódio estabilizado a 3% (AE) e de sistemas adesivos, contendo diferentes solventes orgânicos (acetona ou álcool), sobre a resistência de união ao esmalte humano tratado previamente com peróxido de carbamida a 10% (PC), estabelecendo o padrão de fratura através de microscopia eletrônica de varredura. Quarenta terceiros molares humanos foram selecionados, limpos e armazenados em solução salina de timol a 0,1%. Oitenta fragmentos de 16mm2 foram obtidos das superfícies vestibular e lingual, utilizando-se discos diamantados de dupla-face, em baixa rotação, sob constante irrigação. Os fragmentos foram cobertos com fina camada de cera no7 e embebidos em cilíndro por resina autopolimerizável de poliestireno. Posteriormente, foram divididos aleatoriamente em quatro grupos de acordo com o tipo de tratamento a ser submetido (G1- Saliva, durante todo o experimento; G2- PC, 14 dias/6h, G3- PC, 14dias/6horas + AE após o clareamento, 4dias/7horas e G4- PC, 14dias/6h e AE, durante o clareamento, 2horas). Iniciou-se o tratamento clareador no G3, 4 dias antes dos demais. Os quatro grupos foram subdivididos em oito grupos de acordo com o tratamento restaurador (G1SB, G2SB, G3SB e G4SB- Single Bond + TPH e G1NT, G2NT, G3NT e G4NT- Prime&BondNT + TPH). Finalizado o tratamento restaurador, os fragmentos foram imediatamente preparados para o ensaio de microtração. Cortes seriados foram realizados em cada amostra para obtenção de duas fatias centralizadas de, aproximadamente, 1mm de espessura. Posteriormente, com auxílio de uma broca 1093FF, foi confeccionado em cada fatia, uma constricção, com área adesiva de, aproximadamente, 1mm2, em forma de ampulheta. Os testes de microtração foram realizados em máquina de ensaio Universal, com velocidade de 0,5mm/min. ANOVA e teste de Tukey indicaram que não houve diferença estatística entre os grupos não clareados e os clareados tratados com ascorbato de sódio estabilizado a 3%. Entretanto, para o grupo clareado apenas, a resistência de união foi significantemente diminuída. Para o fator adesivo, não houve diferença estatisticamente significante entre Single Bond e Prime&BondNT. Nas observações em MEV, foi verificada presença de bolhas no adesivo Prime&BondNT do grupo clareado. Os padrões de fratura demonstraram maior número de falhas coesivas nos materiais resinosos submetidos ao clareamento. O gel de ascorbato de sódio estabilizado a 3%, independente da técnica de uso, foi capaz de melhorar os valores de resistência de união ao esmalte clareado / Abstract: The purpose of this in vitro study was to evaluate the effect of a 3% sodium ascorbate gel stabilized (AE) as well as of adhesive organic solvents derived from alcohol or acetone onto the bond strength to human enamel previously treated with carbamide peroxide at 10%, defining the fracture pattern by electronic scanning microscopy. Forty human third molars were selected, cleaned, and kept in saline solution of timol at 0,1%. Eighty fragments of 16mm2 were obtained by the use of double-face diamond discs, in low rotation, under constant irrigation, perpendicularly to buccal and lingual surfaces. The fragments were relieved with a thin layer of wax n° 7 and steep in a cylinder by a self-curing polyester resin. Afterwards, they were random divided into four groups according to the type of bleaching technique to be employed (G1-saliva, G2-PC for 14 days, G3-PC + AE after bleaching for 7 daily hours, during 4 days and G4- PC and AE during bleaching, daily during 2 hours). The four groups were subdivided into eight groups according to the restorative technique (G1A, G2A, G3A and G4A - Single Bond (SB) + TPH and G1B, G2B, G3B and G4B - Prime&BondNT (NT) + TPH). Bleaching treatment was started in the G3, four days before the other groups. Concluded the restorative treatment, the fragments were immediately prepared for micro-traction procedure. Serial cuts were performed in each sample to obtain two centralized slices 1mm thick. Afterwards, using a 1093 FF drill, an hour-glass was done in each slice, with adhesive area of approximately 1mm2. The microtensile tests were performed in an Universal essay machine, at 0,5 mm/min speed. ANOVA and Tukey test indicated that there wasn¿t statistical difference between non-bleached groups and the bleached ones treated with sodium ascorbate at 3%. However, for the group just bleached, the bond strength was significantly decreased. Regarding the adhesive factor, there was not statistically significant difference between SB and NT. On Electronic Scanning Microscopy observations, it was detected the presence of bubbles in the adhesive NT of the bleached group. The fracture standards demonstrated higher number of cohesive failures in the resinous materials undergone to bleaching / Mestrado / Dentística / Mestre em Clínica Odontológica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289120
Date30 March 2005
CreatorsSilva, Ana Paula Brito da
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Marchi, Giselle Maria, 1970-, Rodrigues, Jose Augusto, Correr Sobrinho, Lourenço
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format91f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds