An experimental investigation to study the influence of base metal composition on the time required to achieve complete isothermal solidification (tf) during TLP bonding of three Ni-base superalloys was performed. Alloys IN 738, DS Rene80 and DS IC 6 show similar behaviour when bonded at 1100 oC, with comparable tf. However, at higher temperatures, IN 738 requires extended period of time (as compared to DS Rene80 and DS IC 6) to achieve complete isothermal solidification. The prolonged tf in IN 738 appears to be caused by a more pronounced reduction in concentration gradient of the diffusing solute within the material during bonding. In contrast, the shorter complete isothermal solidification time experienced by alloy DS IC6 is attributable to its capability to better accommodate the diffusing solute, through the formation of densely packed second-phase precipitates in the diffusion affected zone (DAZ).
| Identifer | oai:union.ndltd.org:MANITOBA/oai:mspace.lib.umanitoba.ca:1993/22072 |
| Date | 22 August 2013 |
| Creators | Hunedy, Juhaina |
| Contributors | Ojo, Olanrewaju (Mechanical & Manufacturing Eng.), Richards, Norman (Mechanical & Manufacturing Eng.) Hashemian, Fariborz (Civil Eng.) |
| Source Sets | University of Manitoba Canada |
| Detected Language | English |
Page generated in 0.0038 seconds